Effective Thermal Conductivity Of Mof-5 Powder Under A Hydrogen Atmosphere

Hui Wang,Zhiguo Qu,Wen Zhang,Wen-Quan Tao

DOI: https://doi.org/10.3390/computation3040558

2015-01-01

Computation

Abstract:Effective thermal conductivity is an important thermophysical property in the design of metal-organic framework-5 (MOF-5)-based hydrogen storage tanks. A modified thermal conductivity model is built by coupling a theoretical model with the grand canonical Monte Carlo simulation (GCMC) to predict the effect of the H-2 adsorption process on the effective thermal conductivity of a MOF-5 powder bed at pressures ranging from 0.01 MPa to 50 MPa and temperatures ranging from 273.15 K to 368.15 K. Results show that the mean pore diameter of the MOF-5 crystal decreases with an increase in pressure and increases with an increase in temperature. The thermal conductivity of the adsorbed H-2 increases with an increased amount of H-2 adsorption. The effective thermal conductivity of the MOF-5 crystal is significantly enhanced by the H-2 adsorption at high pressure and low temperature. The effective thermal conductivity of the MOF-5 powder bed increases with an increase in pressure and remains nearly unchanged with an increase in temperature. The thermal conductivity of the MOF-5 powder bed increases linearly with the decreased porosity and increased thermal conductivity of the skeleton of the MOF-5 crystal. The variation in the effective thermal conductivities of the MOF-5 crystals and bed mainly results from the thermal conductivities of the gaseous and adsorption phases.