Abstract:Porosity-controllable TiO2 nanocrystallines with pure anatase phase have been synthesized through a salt-leaching assisted sol-gel method, where glycerol was used as the dispersant to disperse the inorganic precursor (tetrabutyl titanate, TBT) and the chelating ligand to attenuate the hydrolysis/condensation reaction kinetics, while the salts (NaCl) were used as porosity-induced agents to produce pores in the final titania products when the salts leached out. The porosities and surface areas of obtained titania samples could be adjusted by altering the NaCl concentration in the precursor sol, which was examined by experimental techniques such as XRD, TEM and Brunauer-Emmett-Teller (BET) nitrogen adsorption-desorption. In addition, their photocurrent actions and photocatalytic abilities were also investigated so as to address the relationship between the nanostructures and their photoelectrochemical properties. It was demonstrated that the obtained titania samples exhibited different photocurrent actions and photocatalytic activities due to their different morphologies, particle sizes, surface areas as well as pore architectures. Therefore, the salt-leaching assisted sol-gel method described herein offers a new effective and facile strategy for the preparation of pure anatase TiO2 nanocrystallines with adjustable porosity, as well as provides the titania products with specific photoelectrochemical properties for applications in a variety of areas such as photovoltaic cells, photocatalysis and so on.

Water-assisted crystallization of mesoporous anatase TiO2 nanospheres.

Rapid-Heating-Triggered in Situ Solid-State Transformation of Amorphous TiO2 Nanotubes into Well-Defined Anatase Nanocrystals

In-Situ Anatase Flake Crystals Prepared By Sol-Gel Method At Low Temperature

Self-assembly and Photocatalysis of Mesoporous TiO 2 Nanocrystal Clusters

Low‐Temperature Transformation of Titania Thin Films from Amorphous Nanowires to Crystallized Nanoflowers for Heterogeneous Photocatalysis

Crystallization of Anatase from Amorphous Titania in Hot Water and in Vitro Biomineralization.

Room‐Temperature Hydrolysis of Potassium Titanyl Oxalate and Water‐Assisted Crystallization for TiO2 with High Photocatalytic Activity

Direct Continuous Hydrothermal Synthesis of High Surface Area Nanosized Titania

Mesoporous TiO2 Single-Crystal Particles from Controlled Crystallization-Driven Mono-Micelle Assembly As an Efficient Photocatalyst.

Review of Water-Assisted Crystallization for TiO2 Nanotubes

New Mechanistic Insight of Low Temperature Crystallization of Anodic TiO2 Nanotube Array in Water

Effects of Water Amount and Ph on the Crystal Behavior of a TiO2 Nanocrystalline Derived from a Sol–Gel Process at a Low Temperature

Ordered Mesoporous Thin Films Of Rutile Tio2 Nanocrystals Mixed With Amorphous Ta2o5

Synthesis Of Nanocrystalline Tio2 By A Salt-Leaching Assisted Sol-Gel Method And Their Photoelectrochemical Properties

Review of Water-Assisted Crystallization for TiO 2 Nanotubes

Ammonium Acetate And Ethylenediamine-Assisted Synthesis Of Anatase Nanocrystals With {0 10} Facets And Enhanced Photocatalytic Activity

Facile Synthesis and Active Photocatalysis of Mesoporous and Microporous Tio2 Nanoparticles

Nanoporous Anatase TiO2 Mesocrystals: Additive-Free Synthesis, Remarkable Crystalline-Phase Stability, and Improved Lithium Insertion Behavior.

Mesoporous TiO2 Microspheres with Precisely Controlled Crystallites and Architectures

Preparation of Nanocrystalline Anatase Tio2 Using Basic Sol-Gel Method

A Novel Approach to Synthesis of High-Dispersed Anatase Titania Nanocrystals