Galvanic Replacement Synthesis of AgxAu1−x@CeO2 (0 ≤ X ≤ 1) Core@shell Nanospheres with Greatly Enhanced Catalytic Performance

Dapeng Liu,Wang Li,Xilan Feng,Yu Zhang

DOI: https://doi.org/10.1039/c5sc02774h

IF: 8.4

2015-01-01

Chemical Science

Abstract:A galvanic replacement strategy has been successfully adopted to design AgxAu1−x@CeO2 core@shell nanospheres derived from Ag@CeO2 ones.

What problem does this paper attempt to address?

ment synthesis of Ag x Au 1 x @ CeO 2 ( 0 # x # 1 ) core @ shell nanospheres with greatly enhanced catalytic performance †

Dapeng Liu,Wang Li,Xilan Fenga,Yu Zhang

2015-01-01

Abstract:A galvanic replacement strategy has been successfully adopted to design AgxAu1 x@CeO2 core@shell nanospheres derived from Ag@CeO2 ones. After etching using HAuCl4, the Ag core was in situ replaced with AgxAu1 x alloy nanoframes, and void spaces were left under the CeO2 shell. Among the as-prepared AgxAu1 x@CeO2 catalysts, Ag0.64Au0.36@CeO2 shows the optimal catalytic performance, whose catalytic efficiency reaches even 2.5 times higher than our previously reported Pt@CeO2 nanospheres in the catalytic reduction of 4-nitrophenol (4-NP) by ammonia borane (AB). Besides, Ag0.64Au0.36@CeO2 also exhibits a much lower 100% conversion temperature of 120 C for catalytic CO oxidation compared with the other samples.
Galvanic Replacement-Free Deposition of Au on Ag for Core-Shell Nanocubes with Enhanced Chemical Stability and SERS Activity.

Yin Yang,Jingyue Liu,Zheng-Wen Fu,Dong Qin

DOI: https://doi.org/10.1021/ja502472x

IF: 15

2014-01-01

Journal of the American Chemical Society

Abstract:We report a robust synthesis of Ag@Au core-shell nanocubes by directly depositing Au atoms on the surfaces of Ag nanocubes as conformal, ultrathin shells. Our success relies on the introduction of a strong reducing agent to compete with and thereby block the galvanic replacement between Ag and HAuCl4. An ultrathin Au shell of 0.6 nm thick was able to protect the Ag in the core in an oxidative environment. Significantly, the core-shell nanocubes exhibited surface plasmonic properties essentially identical to those of the original Ag nanocubes, while the SERS activity showed a 5.4-fold further enhancement owing to an improvement in chemical enhancement. The combination of excellent SERS activity and chemical stability may enable a variety of new applications.
A General One-Pot Strategy for the Synthesis of Au@multi-oxide Yolk@shell Nanospheres with Enhanced Catalytic Performance.

Jian Li,Shuyan Song,Yan Long,Shuang Yao,Xin Ge,Lanlan Wu,Yibo Zhang,Xiao Wang,Xiangguang Yang,Hongjie Zhang

DOI: https://doi.org/10.1039/c8sc01520a

IF: 8.4

2018-01-01

Chemical Science

Abstract:By integrating redox self-assembly and redox etching processes, we report a general one-pot strategy for the synthesis of Au@multi-M x O y (M = Co, Ce, Fe, and Sn) yolk@shell nanospheres. Without any additional protecting molecule or reductant, the whole reaction is a clean redox process that happens among the inorganic metal salts in an alkaline aqueous solution. By using this method, Au@Co3O4/CeO2 (Au@Co-Ce), Au@Co3O4/Fe2O3 (Au@Co-Fe), and Au@CeO2/SnO2 (Au@Ce-Sn) yolk@shell nanospheres with binary oxides as shells, Au@Co3O4/CeO2/Fe2O3 (Au@Co-Ce-Fe) yolk@shell nanospheres with ternary oxides as shells and Au@Co3O4/CeO2/Fe2O3/SnO2 (Au@Co-Ce-Fe-Sn) yolk@shell nanospheres with quaternary oxides as shells can be obtained. Subsequently, the catalytic CO oxidation was selected as the catalytic model, and the Au@Co-Ce system was chosen as the catalyst. It was found that the catalytic activity of Au@Co-Ce yolk@shell nanospheres can be optimized by altering the relative proportion of Co and Ce oxides.
Synthesis and Properties of CeO2 @Au Core-Shell Structure Nanoparticles

Xiaofeng Yang,Xiangting Dong,Lei Huang,Jinxian Wang,Guixia Liu

DOI: https://doi.org/10.3321/j.issn:1000-4343.2008.06.003

2008-01-01

Abstract:Spherical CeO2 nanoparticles were prepared by precipitation method.The CeO2@Au core-shell nanoparticles were synthesized by chemical reduction of [AuCl4]-on the surface of as-prepared CeO2 colloids using the sodium citrate as reducing agent.The TEM images showed that the CeO2 nanoparticles were well dispersed and the particle diameter was about 5 nm.The CeO2@Au core-shell nanoparticles had perfectly spherical shape with a narrow size distribution,non-agglomeration and the average particle size was about 15 nm.According to the XRD results,the CeO2@Au core-shell was crystalline and cubic in structure with space group O5H-FM3M of CeO2,space group Fm-3m of Au.The UV-vis results demonstrated that the two strong absorption spectrum were observed corresponding to the surface plasma band of the respective metal oxide and metal(viz.300 nm for CeO2 and 520 nm for Au in CeO2@Au core-shell nanoparticles).The EDS analysis confirmed the presence of Ce,O and Au elements in core-shell structured CeO2@Au nanoparticles.According to the difference of Ce3d3/2 and Au4f orbital electron binding energy in XPS between experimental binding energy and standard binding energy,it could be inferred that there existed an interaction between Au and CeO2.
Fabrication Of Ag-Ceo2 Core-Shell Nanospheres With Enhanced Catalytic Performance Due To Strengthening Of The Interfacial Interactions

Jun Zhang,Liping Li,Xinsong Huang,Guangshe Li

DOI: https://doi.org/10.1039/c2jm16701h

2012-01-01

Journal of Materials Chemistry

Abstract:Interfacial interactions are often found in human medical devices, hybrid solar cells, and catalysis. However, there is a lack of control of these interactions when tailoring the materials properties for many technological applications. As a case study, we reported on the synthesis of Ag-CeO2 core-shell nanospheres with the aim of strengthening the interfacial interactions to give enhanced catalytic performance. All core-shell nanospheres were synthesized by a surfactant-free method with a subsequent annealing redox reaction. Systematic sample characterizations indicate that metallic Ag cores with a diameter of 50-100 nm were wrapped by assembled nanoparticles of CeO2 with a shell thickness of 30-50 nm to form a nano-scale core-shell structure. The interfacial interactions between the Ag core and CeO2 shell were strengthened by annealing, surprisingly, as followed by generation of oxygen vacancies to provide abundant of absorption sites for oxygen species. As a consequence, the temperature for oxygen spilling was lowered to 79 degrees C, and the catalytic performance was abnormally enhanced, as indicated by complete CO oxidation at 120 degrees C with no sign of deactivation, even when the reaction time is beyond 100 h. The reaction products were desorbed quickly from the surfaces of the core-shell nanospheres, which accounts for their superior stability during catalytic reactions.
Co3O4@CeO2 Core@Shell Cubes: Designed Synthesis and Optimization of Catalytic Properties

Jiangman Zhen,Xiao Wang,Dapeng Liu,Shuyan Song,Zhuo Wang,Yinghui Wang,Junqi Li,Fan Wang,Hongjie Zhang

DOI: https://doi.org/10.1002/chem.201304109

2014-01-01

Abstract:AbstractMastery of nanomaterial structure enables the control of its properties to enhance its performance for a given application. Herein, we demonstrate a fast and facile self‐assembly method for the synthesis of a series of Co3O4@CeO2 core@shell cubes, which are characterized by SEM, TEM, XRD, inductively coupled plasma mass spectrometry (ICP‐MS), and X‐ray photoelectron spectroscopy (XPS) analyses. The results indicate that the thickness of the CeO2 shell can be tuned through simple variation of the feeding molar ratio of Ce/Co. These Co3O4@CeO2 core@shell cubes are used for catalytic CO oxidation and show good catalytic properties. Moreover, the relationship between the catalytic performance and the CeO2 shell thickness is studied in depth to optimize the catalytic properties.
Co(3)O(4)@CeO(2) core@shell cubes: designed synthesis and optimization of catalytic properties.

Jiangman Zhen,Xiao Wang,Dapeng Liu,Shuyan Song,Zhuo Wang,Yinghui Wang,Junqi Li,Fan Wang,Hongjie Zhang

DOI: https://doi.org/10.1002/chem.201304109

2014-01-01

Abstract:Mastery of nanomaterial structure enables the control of its properties to enhance its performance for a given application. Herein, we demonstrate a fast and facile self-assembly method for the synthesis of a series of Co3 O4 @CeO2 core@shell cubes, which are characterized by SEM, TEM, XRD, inductively coupled plasma mass spectrometry (ICP-MS), and X-ray photoelectron spectroscopy (XPS) analyses. The results indicate that the thickness of the CeO2 shell can be tuned through simple variation of the feeding molar ratio of Ce/Co. These Co3 O4 @CeO2 core@shell cubes are used for catalytic CO oxidation and show good catalytic properties. Moreover, the relationship between the catalytic performance and the CeO2 shell thickness is studied in depth to optimize the catalytic properties.
Synthesis of a Hollow Structured Core–shell Au@CeO2–ZrO2 Nanocatalyst and Its Excellent Catalytic Performance

Chenhao Du,Yun Guo,Yanglong Guo,Xue-Qing Gong,Guanzhong Lu

DOI: https://doi.org/10.1039/c7ta00015d

IF: 11.9

2017-01-01

Journal of Materials Chemistry A

Abstract:We proposed a hard-templated and electrostatic attraction induced deposition method to prepare a hollow core–shell Au@CeO2–ZrO2 nanocatalyst with a high surface area, in which a 6–8 nm ultrathin layer composed of CeO2–ZrO2 nanocrystals is embedded with individual Au nanoparticles, forming a sub-10 nm core–shell-like structure.
Ce0.9fe0.1o1.97/Ag: A Cheaper Inverse Catalyst with Excellent Oxygen Storage Capacity and Improved Activity Towards Co Oxidation

Ying Zuo,Liping Li,Xinsong Huang,Guangshe Li

DOI: https://doi.org/10.1039/c3cy00722g

IF: 6.177

2014-01-01

Catalysis Science & Technology

Abstract:Noble-metal-supported metal oxides (e. g., Au/CeO2, Pd/Al2O3, etc.) are popular as efficient catalysts for many important catalytic reactions, while their high price and easy deactivation restrict their broad application. Herein, we initiate a double substitution methodology to acquire catalysts with merits of excellent catalytic activity, high stability, and relatively low cost. For this purpose, a Au/CeO2 catalyst was used as reference, and the noble metal Au was completely replaced by the cheaper Ag, meanwhile the rare earth ion, Ce4+ of the CeO2 support was partially substituted by the transition metal ion, Fe3+. This inversely supported catalyst, Ce0.9Fe0.1O1.97/Ag, was prepared by a two-step method based on co-precipitation and a subsequent liquid-phase reduction. Systematic characterizations demonstrate that Ag nanoparticles with a diameter of around 50 nm were wrapped by Ce0.9Fe0.1O1.97 layers. Between the Ag nanoparticles and Ce0.9Fe0.1O1.97 layer, there existed a strong interaction. When this sample was tested as a catalyst for CO oxidation, a full conversion temperature of 150 degrees C was achieved at a space velocity of 24 000 ml h(-1) g(-1) cat, showing a catalytic activity comparable to that previously reported in the literature on the known catalyst Au@CeO2 measured at a lower space velocity of 15 000 ml h(-1) g(-1) cat. More strikingly, this catalyst showed a superb catalytic stability and enhanced oxygen storage capacity. The introduction of smaller F-e3+ into the CeO2 lattice and the strong interactions between Ag and Ce0.9Fe0.1O1.97 strongly improved the stability and catalytic performance.
The Synthesis of SiO2@AuAg@CeO2 Sandwich Structures with Enhanced Catalytic Performance Towards CO Oxidation

Hongxiao Yang,Wei Liu,Zhaohui Wang,Guoxin Sun

DOI: https://doi.org/10.1002/slct.201901792

2019-01-01

ChemistrySelect

Abstract:Novel sandwich structure SiO2@AuAg@CeO2 nanospheres (SACs), as low-temperature CO oxidation catalysts, were designed and prepared in this work. The SACs include SiO2 nanosphere support, embedded bimetallic AuAg nanoparticles, and CeO2 shell. The transmission electron microscope (TEM), elemental mapping images, and ultraviolet-visible (UV-vis) spectroscopy indicated the successful fabrication of the SACs sandwich structure. The catalytic performance of SACs varies with the AuAg composition and achieves the best catalytic activity when Au/Ag atomic ratio is 2:1. The strong synergistic effect of AuAg alloy remarkably promotes the CO oxidation through facilitating the adsorption of CO and O-2 on the AuAg nanoparticles. The CeO2 non-compact shell not only provides effective protection for AuAg nanoparticles from aggregation but also gives CO full access to the catalysts. With unique sandwich structure and specific chemical composition, the SiO2@Au2Ag1@CeO2 nanospheres with CeO2 shell thickness of 5 nm present excellent low-temperature catalytic activity and high-temperature thermal stability.
Decoration of Pt on Cu/Co double-doped CeO<sub>2</sub> nanospheres and their greatly enhanced catalytic activity

Fan Wang,Wang Li,Xilan Feng,Dapeng Liu,Yu Zhang

DOI: https://doi.org/10.1039/c5sc04069h

IF: 8.4

2016-01-01

Chemical Science

Abstract:In this paper, we report an efficient strategy for the synthesis of Cu/Co double-doped CeO2 nanospheres (CuxCo1−x–CeO2–Pt, 0 ≤ x ≤ 1), which were fabricated via a simple water–glycol system.
Synthesis of monodispere Au@Co3O4 core-shell nanocrystals and their enhanced catalytic activity for oxygen evolution reaction.

Zhongbin Zhuang,Wenchao Sheng,Yushan Yan

DOI: https://doi.org/10.1002/adma.201400336

IF: 29.4

2014-01-01

Advanced Materials

Abstract:Novel OER catalysts - monodisperse Au@Co3O4 core-shell nanocrystals - have been prepared by synthesizing Au nanocrystals, followed by deposition of Co shells and their conversion to Co3O4 shells. Owing to the synergistic effect, Au@Co3O4 nanocrystals have an OER activity 7 times as high as a Au and Co3O4 nanocrystals mixture or Co3O4 nanocrystals alone, and 55 times as high as Au nanocrystals alone.
Controllable Synthesis and Enhanced Electrochemical Properties of Multifunctional AucoreCo3O4shell Nanocubes

Jianqiang Hu,Zhenhai Wen,Qiang Wang,Xin Yao,Qian Zhang,Jianhua Zhou,Jinghong Li

DOI: https://doi.org/10.1021/jp063216h

2006-01-01

Abstract:Multifunctional AucoreCo3O4shell nanocubes were synthesized through the introduction of chloroauric acid (HAuCl4) into a typical hydrothermal system after a solvothermal process was completed to form metastable Co3O4 hollow nanospheres in the presence of sodium dodecyl benzenesulfonate (SDBS), which served as the surfactant. The strategy suggested that HAuCl4 played a vital role in the shape transformation and core/shell structure formation, and the sizes of the nanocubes can be tunable through control of the acid concentration. The core/shell structure of the nanocubes was demonstrated by X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), and element analysis (EA) measurements. Moreover, Li ion battery measurement indicated that trace Au intercalation altered not only the size and shape of the Co3O4 nanoparticles but also greatly increased their electrochemical properties. These multifunctional nanocubes will be not only helpful to study physical chemistry properties of magnetic nanocrystals but also are expected to find use in many fields such as biomolecular detection and analysis, sensor, electrochemistry, and Li ion batteries.
Ag/Au-decorated Fe3O4/SiO2 composite nanospheres for catalytic applications

Ling Li,Eugene S.G. Choo,Xiaosheng Tang,Jun Ding,Junmin Xue

DOI: https://doi.org/10.1016/j.actamat.2010.04.004

IF: 9.4

2010-01-01

Acta Materialia

Abstract:Noble metal particles in nanoscale (Au, Ag, Pt, etc.) have attracted intensive research interest due to their promising catalysis properties. However, the practical applications of these nanoparticle catalysts are always jeopardized by two problems. One is the difficulty in recovering the used nanoparticles and the other arises from the low catalytic efficiency due to the aggregation of the nanoparticles. In this work, Ag/Au nanoparticles were distributed onto spherical superparamagnetic carriers (SSCNs), which were fabricated through a facile oil-in-DEG emulsion route. The Ag/Au nanoparticles were attached onto the SSCNs by two steps. The Au seeds were attached onto the silica surface through electrostatic attraction first, and the Ag nanoparticles were grown on the basis of the Au seeds. The obtained Ag/Au–SSCN composite nanospheres demonstrated promising catalytic properties, which could also be recycled very easily by using a magnet.
Thiosulfate-mediated Seeded Growth of Au@AuAg Yolk-Shell Nanocubes with Surface Concavity: Optical and Catalytic Properties

Yuanyuan Min,Xiaoyu Li,Yingying Wang,Yan Zhao,Feng Liu,Maochang Liu,Yiqun Zheng

DOI: https://doi.org/10.1039/d3ce00717k

IF: 3.756

2023-01-01

CrystEngComm

Abstract:Gold-silver (Au-Ag) nanocrystals with a combination of concave surface and hollow interior are of great interest due to their distinctive structural merits. Herein, we introduce a facile strategy based on seed surface doping to create concave Au@AuAg yolk-shell nanocubes with surface concavity (Au@AuAg YSCNCs), and examine their intriguing properties in optics and catalysis. In particular, the Au@Ag core-shell nanocubes are generated and reacted with sodium thiosulfate, followed by the addition of HAuCl4 to remove Ag atoms on the side walls and deposit Au/Ag atoms on the corners/edges via the galvanic replacement reaction. UV-vis extinction spectra show that compared to Au@Ag core-shell nanocubes, the current Au@AuAg YSCNCs enable a redshift in the major absorption peak, which should be attributed to the increase in charge polarization regions. Meanwhile, the structural advantage is validated using the reduction of 4-nitrophenol as the model reaction. In particular, the current Au@AuAg YSCNCs exhibit an enhanced catalytic efficiency compared to the Au@Ag core-shell nanocubes. Mechanism study using density functional theory reveals that the structural advantage boosts the catalytic activity by upshifting the d-band center and thus lowering the activation barrier. The current study provides a feasible strategy to integrate two structural features (e.g., concave surface and hollow interior) into one AuAg nano-entity, which could be potentially extended to other metals and/or alloys. Gold@gold-silver (Au@AuAg) yolk-shell nanocubes with surface concavity were prepared via a thiosulfate-mediated galvanic replacement reaction. The nanocubes exhibited noticeable enhancement in catalysis arising from the stepped facets.
A Controllable Surface Etching Strategy For Well-Defined Spiny Yolk@Shell Cuo@Ceo2 Cubes And Their Catalytic Performance Boost

Wang Li,Xilan Feng,Zheng Zhang,Xin Jin,Dapeng Liu,Yu Zhang

DOI: https://doi.org/10.1002/adfm.201802559

IF: 19

2018-01-01

Advanced Functional Materials

Abstract:Herein, an effective top-down etching route is presented to in situ fabricate CuO/CeO2 nanohybrids on the surface of Cu2O microcube templates. This method has well taken into account the factors both in thermodynamics and in kinetics, including surface structural nanocrystallization, construction of mesopores, formation of stable core@shell structures, and strengthened synergistic effects, in order to realize the structural design and hence greatly improve catalytic performance caused by surface nanocrystallization of Cu2O cubes. After etched by aid of ammonia and Ce3+ ions the final products are in a well-defined spiny yolk@shell structures, in which the unetched part of Cu2O cubes serves as the core and the shell is composed by the CuO nanothorns encapsulated by CeO2 nanoparticles. Systematical characterizations including scanning electron microscopy, transmission electron microscopy, X-ray diffraction, X-ray photoelectron spectroscopy, H-2-temperature programmed reduction, N-2 sorption, firmly disclose the relationship between the catalytic properties and the structures of samples. By simply tuning the usage amount of ammonia and Ce3+ ions, the samples show a typical volcano curve in the model reaction of catalytic CO oxidation. Sample CuO@CeO2 center dot 0.05 exhibits the optimal catalytic activity and stability. It is believed that this top-down strategy has shown promising future to design high-performance catalysts for the practical need of application.
Au@Ag core-shell nanocubes with finely tuned and well-controlled sizes, shell thicknesses, and optical properties.

Yanyun Ma,Weiyang Li,Eun Chul Cho,Zhiyuan Li,Taekyung Yu,Jie Zeng,Zhaoxiong Xie,Younan Xia

DOI: https://doi.org/10.1021/nn102237c

IF: 17.1

2010-01-01

ACS Nano

Abstract:This paper describes a facile method for generating Au@Ag core-shell nanocubes with edge lengths controllable in the range of 13.4-50 nm. The synthesis involved the use of single-crystal, spherical Au nanocrystals of 11 nm in size as the seeds in an aqueous system, with ascorbic acid serving as the reductant and cetyltrimethylammonium chloride (CTAC) as the capping agent. The thickness of the Ag shells could be finely tuned from 1.2 to 20 nm by varying the ratio of AgNO(3) precursor to Au seeds. We also investigated the growth mechanism by examining the effects of seeds (capped by CTAC or cetyltrimethylammonium bromide(CTAB)) and capping agent (CTAC vs CTAB) on both size and shape of the resultant core-shell nanocrystals. Our results clearly indicate that CTAC worked much better than CTAB as a capping agent in both the syntheses of Au seeds and Au@Ag core-shell nanocubes. We further studied the localized surface plasmon resonance properties of the Au@Ag nanocubes as a function of the Ag shell thickness. By comparing with the extinction spectra obtained from theoretical calculations, we derived a critical value of ca. 3 nm for the shell thickness at which the plasmon excitation of the Au cores would be completely screened by the Ag shells. Moreover, these Au@Ag core-shell nanocubes could be converted into Au-based hollow nanostructures containing the original Au seeds in the interiors through a galvanic replacement reaction.
Functional CeO x nanoglues for robust atomically dispersed catalysts

Xu Li,Xavier Isidro Pereira-Hernández,Yizhen Chen,Jia Xu,Jiankang Zhao,Chih-Wen Pao,Chia-Yu Fang,Jie Zeng,Yong Wang,Bruce C. Gates,Jingyue Liu

DOI: https://doi.org/10.1038/s41586-022-05251-6

IF: 64.8

2022-01-01

Nature

Abstract:Single-atom catalysts 1 make exceptionally efficient use of expensive noble metals and can bring out unique properties 1 – 3 . However, applications are usually compromised by limited catalyst stability, which is due to sintering 3 , 4 . Although sintering can be suppressed by anchoring the metal atoms to oxide supports 1 , 5 , 6 , strong metal–oxygen interactions often leave too few metal sites available for reactant binding and catalysis 6 , 7 , and when exposed to reducing conditions at sufficiently high temperatures, even oxide-anchored single-atom catalysts eventually sinter 4 , 8 , 9 . Here we show that the beneficial effects of anchoring can be enhanced by confining the atomically dispersed metal atoms on oxide nanoclusters or ‘nanoglues’, which themselves are dispersed and immobilized on a robust, high-surface-area support. We demonstrate the strategy by grafting isolated and defective CeO x nanoglue islands onto high-surface-area SiO 2 ; the nanoglue islands then each host on average one Pt atom. We find that the Pt atoms remain dispersed under both oxidizing and reducing environments at high temperatures, and that the activated catalyst exhibits markedly increased activity for CO oxidation. We attribute the improved stability under reducing conditions to the support structure and the much stronger affinity of Pt atoms for CeO x than for SiO 2 , which ensures the Pt atoms can move but remain confined to their respective nanoglue islands. The strategy of using functional nanoglues to confine atomically dispersed metals and simultaneously enhance their reactivity is general, and we anticipate that it will take single-atom catalysts a step closer to practical applications.
Functional CeOx nanoglues for efficient and robust atomically dispersed catalysts

Jingyue Liu,Xu Li,Xavier Isidro Pereira Hernandez,Chia-Yu Fang,Yizhen Chen,Jie Zeng,Yong Wang,Bruce Gates

DOI: https://doi.org/10.21203/rs.3.rs-604924/v1

2021-01-01

Abstract:Abstract Single-atom catalysts (SACs) exhibit unique catalytic property and maximum atom efficiency of rare, expensive metals. A critical barrier to applications of SACs is sintering of active metal atoms under operating conditions. Anchoring metal atoms onto oxide supports via strong metal-support bonds may alleviate sintering. Such an approach, however, usually comes at a cost: stabilization results from passivation of metal sites by excessive oxygen ligation—too many open coordination sites taken up by the support, too few left for catalytic action. Furthermore, when such stabilized metal atoms are activated by reduction at elevated temperatures they become unlinked and so move and sinter, leading to loss of catalytic function. We report a new strategy, confining atomically dispersed metal atoms onto functional oxide nanoclusters (denoted as nanoglues) that are isolated and immobilized on a robust, high-surface-area support—so that metal atoms do not sinter under conditions of catalyst activation and/or operation. High-number-density, ultra-small and defective CeOx nanoclusters were grafted onto high-surface-area SiO2 as nanoglues to host atomically dispersed Pt. The Pt atoms remained on the CeOx nanoglue islands under both O2 and H2 environment at high temperatures. Activation of CeOx supported Pt atoms increased the turnover frequency for CO oxidation by 150 times. The exceptional stability under reductive conditions is attributed to the much stronger affinity of Pt atoms for CeOx than for SiO2—the Pt atoms can move but they are confined to their respective nanoglue islands, preventing formation of larger Pt particles. The strategy of using functional nanoglues to confine atomically dispersed metal atoms and simultaneously enhance catalytic performance of localized metal atoms is general and takes SACs one major step closer to practical applications as robust catalysts for a wide range of catalytic transformations
Fabrication of SBA-15 supported Ag@Au-Ag metal-core/alloy-shell nanoparticles for CO oxidation

Lini Yang,Menglu Qi,Mingshang Jin

DOI: https://doi.org/10.1039/c3ce26992b

IF: 3.756

2013-01-01

CrystEngComm

Abstract:Ag@Au-Ag metal-core/alloy-shell nanoparticles were successfully synthesized via the localized galvanic replacement reaction in the channels of SBA-15. Since the nanoparticles were prepared in the channels of SBA-15, the size was restricted to around 7 nm. Such a small size and the alloy shell structure were proved to be beneficial for the catalytic property toward CO oxidation reaction.

Galvanic Replacement Synthesis of AgxAu1−x@CeO2 (0 ≤ X ≤ 1) Core@shell Nanospheres with Greatly Enhanced Catalytic Performance

ment synthesis of Ag x Au 1 x @ CeO 2 ( 0 # x # 1 ) core @ shell nanospheres with greatly enhanced catalytic performance †

Galvanic Replacement-Free Deposition of Au on Ag for Core-Shell Nanocubes with Enhanced Chemical Stability and SERS Activity.

A General One-Pot Strategy for the Synthesis of Au@multi-oxide Yolk@shell Nanospheres with Enhanced Catalytic Performance.

Synthesis and Properties of CeO2 @Au Core-Shell Structure Nanoparticles

Fabrication Of Ag-Ceo2 Core-Shell Nanospheres With Enhanced Catalytic Performance Due To Strengthening Of The Interfacial Interactions

Co3O4@CeO2 Core@Shell Cubes: Designed Synthesis and Optimization of Catalytic Properties

Co(3)O(4)@CeO(2) core@shell cubes: designed synthesis and optimization of catalytic properties.

Synthesis of a Hollow Structured Core–shell Au@CeO2–ZrO2 Nanocatalyst and Its Excellent Catalytic Performance

Ce0.9fe0.1o1.97/Ag: A Cheaper Inverse Catalyst with Excellent Oxygen Storage Capacity and Improved Activity Towards Co Oxidation

The Synthesis of SiO2@AuAg@CeO2 Sandwich Structures with Enhanced Catalytic Performance Towards CO Oxidation

Decoration of Pt on Cu/Co double-doped CeO<sub>2</sub> nanospheres and their greatly enhanced catalytic activity

Synthesis of monodispere Au@Co3O4 core-shell nanocrystals and their enhanced catalytic activity for oxygen evolution reaction.

Controllable Synthesis and Enhanced Electrochemical Properties of Multifunctional AucoreCo3O4shell Nanocubes

Ag/Au-decorated Fe3O4/SiO2 composite nanospheres for catalytic applications

Thiosulfate-mediated Seeded Growth of Au@AuAg Yolk-Shell Nanocubes with Surface Concavity: Optical and Catalytic Properties

A Controllable Surface Etching Strategy For Well-Defined Spiny Yolk@Shell Cuo@Ceo2 Cubes And Their Catalytic Performance Boost

Au@Ag core-shell nanocubes with finely tuned and well-controlled sizes, shell thicknesses, and optical properties.

Functional CeO x nanoglues for robust atomically dispersed catalysts

Functional CeOx nanoglues for efficient and robust atomically dispersed catalysts

Fabrication of SBA-15 supported Ag@Au-Ag metal-core/alloy-shell nanoparticles for CO oxidation