Abstract:For the first time, rare earths were utilized to modify silica (SiO2) for improving the ink-receiving properties of silica/PVA (polyvinyl alcohol) composite films which was coated onto PET (polyethylene terephthalate) substrate. Fourier transform infrared spectra, XPS, scanning electron microscope, Brunauer-Emmett-Teller (BET) surface area measurement, contact angle and mechanical strength tests were used to characterize silica and SiO2/PVA composite films before and after modification by rare earths. The results indicated that the rare earths can effectively modify silica by increasing the oxygen-containing groups, decreasing the pore size and cumulative volume of pores, and narrowing the pore size distribution. The possible mechanism during rare earth-modification of silica may be due to the breakage of Si-O-C bonds which generates the carbon radicals combined with dissolved oxygen in the solution to form C-O/C-OH bonds. However, the detailed reaction mechanism still needs to be investigated and clarified in the future because of the complexity during the reaction. The characterization of SiO2/PVA films illustrates that silica content, compared to rare earth treatment time, has stronger effects on the hydrophilicity enhancement of the films. The tensile strength of SiO2/PVA films rapidly increased from 46.8 MPa to 72.6 MPa when increasing the rare earth treatment time from 0 to 10 h. The ink-receiving properties of SiO2/PVA films were thoroughly examined which illustrated that modification of SiO2 by rare earth up to 10 h can significantly enhance the ink-receiving properties of the composite films in terms of image quality, desiccation time of ink and mechanical strength of films with the optimum SiO2/PVA ratio of 0.3 (by weight). Besides, the thermal stability of composite films containing rare earth modified silica was excellent. Therefore, the SiO2/PVA composite films containing rare earth-modified silica seem to be promising materials for high-performance applications.

Study of the Adsorption Performance and Preparation of Functional Nano-Silica Pigment Particles

A coating of silane modified silica nanoparticles on PET substrate film for inkjet printing

Influence Of Nano-Silica On Properties Of Coatings And Coated Ink-Jet Printing Paper

Non-contact Analysis of the Adsorptive Ink Capacity of Nano Silica Pigments on a Printing Coating Base.

Diffusion Process of an Ink Drop in Core–shell Silica–titania Pigment Particles

Preparation and Microcosmic Structural Analysis of Recording Coating on Inkjet Printing Media

Modification of SiO 2 Nanoparticle-Decorated TiO 2 Nanocomposites with Silane Coupling Agents for Enhanced Opacity in Blue Light-Curable Ink

Colored Nano-Silica and Its Adsorption on Cellulosic Materials

APPLICATION OF NANOMETER SILICA IN TOP COATING OF INK JET PAPER

Study Of Dispersing Properties Of Silica Dioxide Used In Color Ink Jet Paper Coating

ENHANCEMENT OF INK-RECEIVING PROPERTIES OF SIO2/PVA COMPOSITE FILMS BY USING RARE EARTH-MODIFIED SIO2 PARTICLES

High Ink Absorption Performance of Inkjet Printing Based on SiO 2 @al 13 Core-Shell Composites

Surface Modification Methods to Improve UV Inkjet Printing Performance of Ceramic

Study on Nano-SiO<sub>2</sub> Used to Improve the Property of Ink

Novel Waterborne UV-Curable Hyperbranched Polyurethane Acrylate/Silica with Good Printability and Rheological Properties Applicable to Flexographic Ink

Colloidal Silica/Poly(Methacrylsiloxane) Nanocomposite Particles: Synthesis, Characterization, and Application in Toners.

Preparation and Characterization of Neodymium Disilicate Ceramic Ink by Mechanical Grinding

Encapsulation of Organic Pigments Yellow with Nanosilica Particles

Preparation and colloidal dispersion behaviors of silica sol doped with organic pigment

A Novel Approach of Chemical Functionalization on Nano-Scaled Silica Particles

Preparation of Imprinted Polymer with Theophylline on Silica Surface and Its Characteristics