Ultra‐Wide Temperature Stable Dielectrics Based on Bi0.5Na0.5TiO3–NaNbO3 System

Qi Xu,Zhe Song,Wenlin Tang,Hua Hao,Lin Zhang,Millicent Appiah,Minghe Cao,Zhonghua Yao,Zichen He,Hanxing Liu
DOI: https://doi.org/10.1111/jace.13693
IF: 4.186
2015-01-01
Journal of the American Ceramic Society
Abstract:The microstructure, phase structure, ferroelectric, and dielectric properties of (1−x)Bi0.5Na0.5TiO3‐xNaNbO3 [(1−x)BNT‐xNN] ceramics conventionally sintered in the temperature range of 1080°C–1120°C were investigated as a candidate for capacitor dielectrics with wide temperature stability. Perovskite phase with no secondary impurity was observed by XRD measurement. With increasing NN content, (1−x)BNT‐xNN was found to gradually transform from ferroelectric (x = 0–0.05) to relaxor (x = 0.10–0.20) and then to paraelectric state (x = 0.25–0.35) at room temperature, indicated by P–I–E loops analysis, associated with greatly enhanced dielectric temperature stability. For the samples with x = 0.25–0.35, the temperature coefficient of capacitance (TCC) was found <11% in an ultra‐wide temperature range of −60°C–400°C with moderate dielectric constant and low dielectric loss, promising for temperature stable capacitor applications.
What problem does this paper attempt to address?