Abstract:For microelectronic industry, Cu-based substrate and epoxy molding compound (EMC) interface is inherently weak and most likely to delaminate, well-known as a major threat for integrated circuits (ICs) reliability. In this paper, hierarchical whisker-like oxide/Cu cone structure was for the first time to be fabricated by combining electroless plating with heat treatment methods to enhance the interface adhesion between Cu-based substrate and EMC. The surface morphology was characterized by scanning electron microscope (SEM). Result shows that the hierarchical whisker-like oxide/Cu cone film is fine, dense and uniform; Single Cu cone structure is about 3-5 μm in height and 1 μm in root diameter; a layer of whisker-like oxide grows perpendicularly to circular surface of Cu cone, with length ranging from tens to hundreds of nanometers. Adhesion strength between the as-prepared substrates and EMC were measured by button shear test. With consideration of oxidation caused by practical processes (e.g. wire bonding), the interface of EMC and porous oxide formed at 260°C for 5 min was taken as standard sample, representative of practical interface. To further study the effect of whisker-like oxide and Cu cone solely on adhesion performance, whisker-like oxide, porous oxide/Cu cone were investigated as well. Button shear test results reveal that interfacial adhesion strength of EMC and whisker-like oxide, porous oxide/Cu cone, hierarchical whisker-like oxide/Cu cone are 85%, 110% and 162% higher than that of standard interface. Moreover, the mechanism for adhesion improvement was discussed by facture surface observation, failure path assumption and force-displacement curve analysis. Results show that interface of EMC and hierarchical whisker-like oxide/Cu cone exhibits brittle/ductile property with about 3-5 μm thick EMC left on the fracture surface, indicating cohesive failure caused by remarkable mechanical interlocking effect. © 2011 Elsevier Ltd. All rights reserved.

Study on brown oxidation process with imidazole group, mercapto group and heterocyclic compounds in printed circuit board industry

Adhesion improvement of Cu-based substrate and epoxy molding compound interface by hierarchical structure preparation

Enhancing peel strength between liquid crystal polymer and copper with plasma treatment, surface oxidation, and silane coating

Enhanced Reactivity of Electroless Cu Interconnection by Surface Oxidation Pretreatment

Mechanistic Insight into the Janus Green B on Electrochemical Roughening Layer of Copper Foil

A Novel Antioxidation Treatment Method for Micron/Nano Copper Materials in Semiconduct Field

Preparation of electronic-grade CuO for copper electrodeposition of printed circuit boards

Novel fluorobenzimidazole-assisted heat resistant anticorrosion copper surface for high-density interconnected printed circuit boards

Surface Modification of Copper for Adhesion Promotion by Polybenzimidazole

Enhanced Anti-Oxidation Copper-Based Conductive Inks for Low Porosity Copper Films in Power Electronics

Enhancing Interfacial Bonding Between the Copper Foil and Poly-Ether-ether-ketone Film Via Dual Modification Using UV/ozone and Silane Coupling

Effects of hygrothermal ageing and thermal shock on reliability of interfacial adhesion between black oxide coated copper substrate and epoxy resin

Study of PCB Bonding Finger Surface Discoloration

Improvement of performance stability of electrolytic copper foils by bi-component additives

Investigation of the post-treatment process for improving corrosion behaviors and adhesion strength of plasma electrolytic oxidation (PEO) coatings on pure copper

Effect of Cu Lead-Frame Oxidation Time on Cu/EMC Interfaces in Power Devices

An accessible strategy for high-performance copper layer fabrication on polyphenylene oxide substrates via polydopamine functionalization and electroless deposition

An investigation into copper oxidation behavior

Copper conductive adhesives for printed circuit interconnects

Oxidation failure and mechanism of lead frame copper alloys for IC package