Abstract:Magnesium alloys are potentially attractive biodegradable materials. However, their rapid corrosion rate limits their biomedical application. To slow down the rate of biodegradation, a protective calcium-phosphate coating was formed on a magnesium alloy substrate by a hydrothermal method. Scanning electron microscope results showed that the coating consisted of two layers with different crystalline characteristics. The loose outer layer showed a prism-like crystal structure, while the compact inner layer is a dense ultra-fine regular di-pyramid-like structure with an average grain dimension of ∼200 nm. The compositions of the inner layer and outer layer were calcium-deficient hydroxyapatite (Ca-def HA) and dicalcium phosphate (DCPa), respectively. The coating adhered well to the substrate with a thickness of about 15 μm. Immersion in Hank’s solution indicated that the coating could significantly improve the degradation properties of magnesium alloy. The pH of the solution containing the coated samples increased much more slowly than the untreated control. After 8 d immersion, the uncoated sample had corroded seriously while the coated sample was much less corroded. The Ca/P atom ratio in both the layers of the coating increased and the coating was still protecting the substrate. The two layers of the coating corroded differently because of differences in solubility. The outer layer was more severely attacked and many holes were formed on the surface, the inner layer suffered less attack. In addition, a growth of precipitate on the inner layer was observed, indicating that surface bioactivity was improved by the coating. Thus, magnesium alloys coated with a Ca-P coating prepared by a hydrothermal method are promising candidate biodegradable biomaterials, and further investigation of in vivo degradation behavior is suggested.

A Novel Biodegradable Phosphate Coating on AZ31B Alloy

Precipitation Control And Mechanical Property Of Calcium Phosphate-Coated Az31b Alloy For Biomedical Application

Calcium Phosphate Coating on Magnesium Alloy for Modification of Degradation Behavior

Preparing Ca-P Coating on Biodegradable Magnesium Alloy by Hydrothermal Method: in Vitro Degradation Behavior

Optimization of the in Vitro Biodegradability, Cytocompatibility, and Wear Resistance of the AZ31B Alloy by Micro-Arc Oxidation Coatings Doped with Zinc Phosphate

Fabrication of Electroactive Poly(γ‐glutamic Acid) Coating for Improving Corrosion Resistance and Cytocompatibility of Magnesium Alloy

Improvement in corrosion resistance and biocompatibility of AZ31 magnesium alloy by NH2+ ions

A Novel Anti-Corrosion and Antibacterial Integrated MAO/PCNZ Composite Coating on AZ31B Mg Alloy

Preparation of phosphate ion-doped Zn–Fe-layered double hydroxide with corrosion resistance and inducing Ca–P deposition on AZ31 Mg alloy

Corrosion Resistance and Biocompatibility of Calcium Phosphate Coatings with a Micro-Nanofibrous Porous Structure on Biodegradable Magnesium Alloys

Characterization and Degradation Study of Calcium Phosphate Coating on Magnesium Alloy Bone Implant in Vitro

Corrosion resistance of a composite polymeric coating applied on biodegradable AZ31 magnesium alloy

A Study on the Structure and Biomedical Application Characteristics of Phosphate Coatings on ZKX500 Magnesium Alloys

Surface Engineering of Biodegradable Magnesium Alloys for Enhanced Orthopedic Implants.

A Combined Coating Strategy Based on Atomic Layer Deposition for Enhancement of Corrosion Resistance of AZ31 Magnesium Alloy

Degradation and Corrosion Behavior of Electrospun PHBV Coated AZ-31 Magnesium Alloy for Biodegradable Implant Applications

Effect of Strontium-Substituted Calcium Phosphate Coatings Prepared by One-Step Electrodeposition at Different Temperatures on Corrosion Resistance and Biocompatibility of AZ31 Magnesium Alloys

A Biodegradable Coating Based on Self‐Assembled Hybrid Nanoparticles to Control the Performance of Magnesium

Design and characterization of β-tricalcium phosphate-based self-passivating coatings on magnesium alloys

A novel Ca-Mg-P/PDA composite coating of Mg alloys to improve corrosion resistance for orthopedic implant materials

A polyphenol‐induced hydroxyapatite coating modulates corrosion resistance and biocompatibility of magnesium alloys