Hydrothermal Synthesis and Optical Properties of ZnO Nanostructured Films Directly Grown From/on Zinc Substrates
Yueping Fang,Xiaogang Wen,Shihe Yang,Qi Pang,Lu Ding,Jiannong Wang,Weikun Ge
DOI: https://doi.org/10.1007/s10971-005-3563-7
2006-01-01
Journal of Sol-Gel Science and Technology
Abstract:Uniform ZnO nanorods arrays are grown directly from and on Zn foils in pure water under hydrothermal conditions at a relatively low temperature. The nanorods are 80–200 nm in diameter and ∼ 1 μm in length, which grow on the Zn foil along the [001] direction. By changing the pure water to a urea solution, a Zn compound ([Zn5(OH)6(CO3)2], a precursor of ZnO nanoflowers film, is created by self-assembly. The ZnO nanoflowers film can be easily obtained by heating the [Zn5(OH)6(CO3)2] compound in N2 at 350∘C for 5–6 hours. Possible growth processes of the ZnO nanorods arrays and the [Zn5(OH)6(CO3)2] nanoflowers are discussed. Photoluminescence properties of the as-prepared ZnO nanostructures have been measured. The ZnO nanorods array synthesized using our method has minimal defects so that only band-gap emission is observed. However, the ZnO nanoflowers film, obtained by heating the [Zn5(OH)6(CO3)2] nanoflower precursor in N2, is polycrystalline and displays strong defect-related emission.