Preparation and Characterization of Mno.5Zno.5Fe2O4 @Au Composite Nanoparticles and its Anti-Tumor Effect on Glioma Cells

y t li,jing liu,li wang,jia zhang,zi yu wang,yue jiao zhong,dong sheng zhang,zhi qiang gao

DOI: https://doi.org/10.4028/www.scientific.net/AMM.138-139.907

2012-01-01

Applied Mechanics and Materials

Abstract:To explore the preparation method and characters of a new gold nanoshells on maganese-zinc ferrite(Mn0.5Zn0.5Fe2O4@Au) composite nanoparticles. Mn0.5Zn0.5Fe2O4@Au nanoparticles with core/shell structure were synthesized by reduction of Au3+ with trisodium citrate in the presence of Mn0.5Zn0.5Fe2O4 magnetic nanoparticles(MZF-NPs) prepared by improved co-preciption with the character of superparamagnetism and detected by transmission electron microscopy(TEM), scanning electron microscopy(SEM), x-ray diffraction(XRD), energy dispersive spectrometry(EDS) and Marven laser particle size analyzer. Thermodynamic test was used to observe temperature change of various doses of Mn0.5Zn0.5Fe2O4@Au nanoparticles. The cytotoxicity of the Mn0.5Zn0.5Fe2O4@Au composite nanoparticles in vitro was tested by the MTT assay. The therapeutic effect of Mn0.5Zn0.5Fe2O4@Au composite nanoparticles combined with magnetic fluid hyperthermia (MFH) on human glioma cells were evaluated in vitro by an MTT assay.The results indicated that the Mn0.5Zn0.5Fe2O4@Au composite nanoparticles were prepared successfully. The core/shell particles were spherical with exact average diameter of them was 66.9nm.EDS showed each Mn0.5Zn0.5Fe2O4@Au nanoparticle contained Mn, Zn, Fe, O and Au elements, and this proved Au had successfully attached to Mn0.5Zn0.5Fe2O4. The result of thermodynamic test showed that Mn0.5Zn0.5Fe2O4@Au composite nanoparticles could serve as a heating source under alternating magnetic field(AMF) exposure leading to reach their steady temperature(40-45 square). Moreover, Mn0.5Zn0.5Fe2O4@Au composite nanoparticles didn't show cytotoxicity in vitro. The therapeutic result reveals that Mn0.5Zn0.5Fe2O4@Au composite nanoparticles can significantly inhibit the growth of glioma cells.The conclusion was that the self-prepared Mn0.5Zn0.5Fe2O4@Au composite nanoparticles had strong magnetic responsiveness and good power absorption capabilities in the high frequency AMF,then they could suggested to be useful for glioma hyperthemia. Mn0.5Zn0.5Fe2O4@Au composite nanoparticles can not only be directed to tumor region in a given magnetic field more exactly but also produce marked thermotherapy.