Abstract:This paper presents studies on the influence of the chemical structure of (meth)acrylic monomers on the properties of powder coatings based on polyacrylate resins. For this purpose, a wide range of monomers were selected—2-hydroxyethyl methacrylate (HEMA), methyl methacrylate (MMA), n-butyl acrylate (nBA), tert-butyl acrylate (tBA), dodecyl acrylate (DA), ethyl acrylate (EA) and benzyl acrylate (BAZ)—for the synthesis of the polyacrylate resin. The average molecular mass and molecular mass distribution of the synthesized resins were measured by gel permeation chromatography (GPC). The glass transition temperature (Tg) and viscosity of polyacrylate resins were determined by using differential scanning calorimetry (DSC) and a Brookfield viscometer. These parameters were necessary to obtain information about storage stability and behavior during the application of powder clear coatings. Additionally, DSC was also used to checked the course of the low-temperature curing reaction between the hydroxyl group contained in the polyacrylate resin and the blocked polyisocyanate group derived from a commercial agent such as Vestanat B 1358/100. The properties of the cured powder clear coatings were tested, such as: roughness, gloss, adhesion to the steel surface, hardness, cupping, scratch resistance, impact resistance and water contact angle. The best powder clear coating based on the polyacrylate resin L_HEMA/6MMA/0.5nBA/0.5DA was characterized as having good scratch resistance (550 g) and adhesion to the steel surface, a high water contact angle (93.53 deg.) and excellent cupping (13.38 mm). Moreover, its crosslinking density (CD) and its thermal stability was checked by using dynamic mechanical analysis (DMA) and thermogravimetric analysis (TGA).

The Coating Property Study of (Meth)Acrylate Copolymer with Gradient Wettability Surfaces

Seed Semicontinuous Emulsion Multi-Copolymerization of (meth)acrylates with High-Solid Content - Effect of the Operation Conditions

Ph Responsivity and Micelle Formation of Gradient Copolymers of Methacrylic Acid and Methyl Methacrylate in Aqueous Solution

Surface modification through gradient morphology control of polymer blends

The Synthesis of Silica-Sol/Acrylate Copolymer Composite Latexes with a Gradient Concentration in the Radial Direction and Their Adhesive Properties

Study of Kinetic of Emulsion Copolymerization of Methyl Methacrylate/ethyl Acrylate

The Preparation and Surface Properties of Silicone-grafted Acrylic Copolymer Coatings

Synthesis and characterization of poly(vinyl chloride)-g-poly (2-hydroxyethyl methacrylate) copolymers

Correlation between the Chemical Structure of (Meth)Acrylic Monomers and the Properties of Powder Clear Coatings Based on the Polyacrylate Resins

Preparation and Properties of Silicone-Acrylate Copolymer Latex

Synthesis of Polyacrylate Emulsion and the Properties of Ambient Curable Coatings

The Effect of Macromonomer Surfactant Microstructure on Aqueous Polymer Dispersion and Derived Polymer Film Properties

Hydrophilic Surface Modification of Poly(Methyl Methacrylate)/Poly(Methyl Methacrylate‐Co‐Acrylic Acid) Composite Film by Surface Activation

Preparation and Properties of 2-Hydroxypropyl Methacrylate-Alkyl Acrylate Copolymer Net-Works

Regulation of Viscoelastic Properties of Styrene-Butyl Acrylate Copolymer by Functional Monomer

Synthesis and Characterization of Catechol-Containing Polyacrylamides with Adhesive Properties

Core-Shell Emulsion Copolymerization and Characterization of Polysiloxane Bearing Vinylic Function/Acrylate Monomer

Study on Damping Properties of Acrylate Latex Copolymer

Low Dielectric Loss and Infrared Emissivity Coating with Enhanced Mechanical Property by Grafting Modification of EPDM

Dual‐responsive Copolymer Poly(2,2,3,4,4,4‐hexafluorobutyl Methacrylate)‐block‐poly[2‐(dimethylamino)ethyl Methacrylate] Synthesized Via Photoatrp for Surface with Tunable Wettability

UV-curable waterborne epoxy acrylate coating modified by monomethacryloyloxy-terminated fluorinated oligomer