Abstract:CaSi2O2N2:Ce3+/Eu2+phosphors were successfully synthesized via the solid-state reaction method.Photoluminescence properties of Ce3+-doped,Eu2+-doped and Ce3+/Eu2+codoped samples are investigated.CaSi2O2N2:Ce3+phosphors show a broad band centered at 395 nm under 333 nm excitation.Red-shift occurs as the concentration of Ce3+increases.The molar quenching concentration of Ce3+is approximately 1%.CaSi2O2N2:Eu2+phosphors emit a single,intense,and broad emission band centered at 540 nm when excited at 397 nm.The molar quenching concentration of Eu2+is approximately1%.When excited at 333 nm,the codoped samples Ca0.99-2xSi2O2N2:xCe3+,xLi+,0.01Eu2+emit two broad bands centered at 395 nm and 540 nm,respectively.The emission of Eu2+is significantly enhanced by the increase of Ce3+.When Ca0.98-ySi2O2N2:0.01Ce3+,0.01Li+,yEu2+phosphors are excited at 333 nm,two broad bands with peaks at 395 and 540nm are observed.The former band(at 395nm)is weakened when increasing Eu2+content.However,the band at 540 nm reaches the maximum intensity for y=0.004.These suggest effective energy transfer mechanism from Ce3+to Eu2+taking place in the CaSi2O2N2 sample.The efficiency of energy transfer between Ce3+and Eu2+is calculated,and saturation value occurs when the concentration of Eu2+increases to 1%.The resonance-type energy transfer between Ce3+and Eu2+is dipole-dipole interaction mechanism.

Luminescence and Energy-Transfer Properties of Color-Tunable Ca2Mg0.25Al1.5Si1.25O7:Ce(3+)/Eu(2+)/Tb(3+) Phosphors for Ultraviolet Light-Emitting Diodes.

Luminescence Properties And Energy Transfer Of Ce3+,Tb3+-Coactivated-Sialon Phosphors

Spectral Properties of Alkaline Earth Composite Silicate Phosphors for White-LED

Preparation of CaYAl3O7:Ce3+, Tb3+ Blue-Green Phosphors by Sol-Gel Process

Tunable Luminescence of Ce3+/Eu2+ Activated in Single-Phase Li2BaSiO4 Phosphor Via Energy Transfer

A Novel Tunable Blue-Green-emitting CaGdGaAl2O7:Ce3+,Tb3+ Phosphor Via Energy Transfer for UV-excited White LEDs

Synthesis and luminescence properties of Sr3MgSi2O8:Ce3+,Tb3+ for application in near ultraviolet excitable white light-emitting-diodes

Tunable luminescence Y3Al5O12:0.06Ce 3+, xMn2+ phosphors with different charge compensators for warm white light emitting diodes

Luminescence investigation of Lu2MgAl4SiO12:Ce3+ and Ca2+ substituted Lu2MgAl4SiO12:Ce3+ phosphors

Structure and Luminescence Properties of Bi3+ Activated Ca12Al14O32Cl2 Phosphors

Synthesis, Structure, and Photoluminescence Properties of Ce3+ and Tb3+ Doped Alkaline-Earth Silicate Sr2mgsi2o7 Phosphors for Wleds

Photoluminescence Properties and Energy Transfer in Color Tunable BaY2Si3O10:Ce,Tb Phosphors

Luminescent properties and energy transfer mechanism from Tb3+ to Eu3+ in color adjustable nano Ca5(PO4)3(OH): Eu3+,Tb3+ phosphors

A green-yellow phosphor Mg1.94-xAl3.96Si5.04O18: 0.06Ce3+, xTb3+ with thermal anti-quenching property

Luminescence properties of a tunable blue-green-emitting Ca10(PO4)6S:Ce3+,Tb3+ phosphors for UV-excited white LEDs

Codoped Tb3+ and Mn2+ induced tunable emission and energy transfer in Ca19Zn2(PO4)14:Ce3+,Tb3+,Mn2+

Luminescence investigation of Eu2+/Ce3+/Mn2+ doped Y2Mg2Al2Si2O12 phosphors

Optical Properties and Energy Transfer of NaCaPO4:Ce3+,Tb3+ Phosphors for Potential Application in Light‐Emitting Diodes

Luminescence properties and efficient energy transfer investigations of inverse garnet-type Mg 3 Y 2− x − y Ge 3 O 12 : x Tb 3+ , y Eu 3+ multicolor phosphor

Luminescence properties and efficient energy transfer investigations of inverse garnet-type Mg<sub>3</sub>Y<sub>2-<i>x</i>-<i>y</i></sub>Ge<sub>3</sub>O<sub>12</sub >:<i>x</i>Tb<SUP>3+</SUP>, <i>y</i>Eu<SUP>3+</SUP> multicolor phosphor

Luminescence properties of CaSi2O2N2 ∶Ce3+/Eu phosphors