Abstract:Herein, we report the gamma radiation-induced structural, optical, luminescence and radiation shielding characteristics of Na 2 O + ZnO + B 2 O 3 glasses containing CuO with variable doses of gamma radiation up to 90 kGy (i.e. for 30, 60 and 90 kGy). The irradiated glass system was systematically analysed using various characterization techniques such as XRD, RAMAN, UV-Vis-NIR, Photoluminescence and Decay kinetics. It was observed that the density of the glasses increased from 2.400 g/cm 3 to 2.504 g/cm 3 with an increase of radiation dose from unirradiated (0 kGy) to 90 kGy due to the increase of non-bridging oxygens induced during the irradiation. However, the glasses exhibit amorphous characteristics and no significant structural changes up to 90 kGy, as revealed by the XRD and RAMAN spectral analysis. On the other hand, the band gap (indirect) of the glass sample decreases from 3.098 eV to 2.625 eV for un-irradiated to 90 kGy, respectively. Photoluminescence studies reveal that the un-irradiated glass exhibits a broad emission spectrum and is unaltered up to 30 kGy. Further, with an increase in irradiation dose (i.e. 30, 90 kGy), the intensity of the emission peak decreases suddenly, indicating the luminescence quenching. This is due to the formation of more defects and NBOs, which act as electron trapping centres, resulting in the quenching of luminescence. Also, the lifetime of the sample decreases from 33 μs to 20 μs for unirradiated to 90 kGy. The CIE diagram indicates that the emission is in the blue region (unirradiated) and shifts towards the bluish-white region with an increase in gamma dose. Furthermore, we have used Phys-X software (available free online) to evaluate the gamma radiation shielding behaviour of the prepared glasses. We have examined the relationship between the shielding parameters such as, LAC, MAC, HVL and MFP with density (experimental) and the results are presented in detail.

Gamma-ray Irradiation Induced Bulk Photochromism in WO3–P2O5 Glass

Effect of Gamma‐Ray Irradiation on the Optical Properties of PbO–B2O3–SiO2 and Bi2O3–B2O3–SiO2 Glasses

Gamma-ray induced reversible photochromism of Mn 2+ activated borophosphate glasses

Gamma-ray-induced multi-effect on properties of chalcogenide glasses

Broadband infrared luminescence in γ-ray irradiated bismuth borosilicate glasses.

Gamma irradiation effects on photoluminescence and semiconducting properties of non-conventional heavy metal binary PbO–Bi2O3 glasses

Gamma-ray irradiation effects on luminescent glasses for white led applications

Gamma Irradiation Effects on ZnO-based Scintillating Glasses Containing CeO2 And/or TiO2

Irradiation Resistance of Novel Scintillating Glass with Sno2 As Emission Center

Effect of Gamma Exposure on Chalcogenide Glass Films for Microphotonic Devices

Study on optical properties and γ‐ray irradiation resistance of heavy metal oxide tellurite glasses

Study On Optical Properties And Gamma-Ray Irradiation Resistance Of Heavy Metal Oxide Tellurite Glasses

Room-temperature X-ray induced photochromic properties of tungsten oxide

Irradiation Effects on Glasses Containing ZnO As Emission Centers

Radiation-induced transmission spectral variations of Ce3+-doped heavy germanate glasses

Effect of melting atmospheres on the optical property of radiation-hard fluorophosphate glass

Effect of the Addition of WO3 on the Structure and Luminescent Properties of ZnO-B2O3:Eu3+ Glass

Effect of TeO2 on Near‐Infrared Emission from Bismuth Centers in Borogermanate Glasses

Γ-Ray Irradiation Induced Multiple Effects on Ge–As–Se Chalcogenide Glasses

Optical properties, gamma attenuation and fast neutrons moderating performance of V2O5–Bi2O3–B2O3–PbO glasses

Investigation of the Gamma Irradiation-Induced Structural, Optical, Luminescence and Shielding Properties of CuO-Integrated Sodium-Zinc-Borate Glasses