Investigation of the Gamma Irradiation-Induced Structural, Optical, Luminescence and Shielding Properties of CuO-Integrated Sodium-Zinc-Borate Glasses
Areej S. Alqarni,N Srinatha,S Hemalatha,N Suriyamurthy,A Madhu,Upendra Kumar Kagola
DOI: https://doi.org/10.1007/s12633-024-03052-2
IF: 3.4
2024-06-07
Silicon
Abstract:Herein, we report the gamma radiation-induced structural, optical, luminescence and radiation shielding characteristics of Na 2 O + ZnO + B 2 O 3 glasses containing CuO with variable doses of gamma radiation up to 90 kGy (i.e. for 30, 60 and 90 kGy). The irradiated glass system was systematically analysed using various characterization techniques such as XRD, RAMAN, UV-Vis-NIR, Photoluminescence and Decay kinetics. It was observed that the density of the glasses increased from 2.400 g/cm 3 to 2.504 g/cm 3 with an increase of radiation dose from unirradiated (0 kGy) to 90 kGy due to the increase of non-bridging oxygens induced during the irradiation. However, the glasses exhibit amorphous characteristics and no significant structural changes up to 90 kGy, as revealed by the XRD and RAMAN spectral analysis. On the other hand, the band gap (indirect) of the glass sample decreases from 3.098 eV to 2.625 eV for un-irradiated to 90 kGy, respectively. Photoluminescence studies reveal that the un-irradiated glass exhibits a broad emission spectrum and is unaltered up to 30 kGy. Further, with an increase in irradiation dose (i.e. 30, 90 kGy), the intensity of the emission peak decreases suddenly, indicating the luminescence quenching. This is due to the formation of more defects and NBOs, which act as electron trapping centres, resulting in the quenching of luminescence. Also, the lifetime of the sample decreases from 33 μs to 20 μs for unirradiated to 90 kGy. The CIE diagram indicates that the emission is in the blue region (unirradiated) and shifts towards the bluish-white region with an increase in gamma dose. Furthermore, we have used Phys-X software (available free online) to evaluate the gamma radiation shielding behaviour of the prepared glasses. We have examined the relationship between the shielding parameters such as, LAC, MAC, HVL and MFP with density (experimental) and the results are presented in detail.
materials science, multidisciplinary,chemistry, physical