Abstract:The key goals of this study was to investigate the engineering characteristics and microstructure formation pattern of magnesium phosphate cement (MPC) mortar by adding bentonite clay (BC). For this purpose, consecutive dosages of BC were added in place of magnesia for preparing the surrogate specimens and kept in two static curing conditions like air and water for comparing the target objectives. The analytical results indicated that the consecutive increment of BC quantity up to 20% exhibited the satisfactory level of water absorption reduction, strength activity indices (SAI) and strength retention coefficient, where 10% and 15% BC contents greatly improved the density, porosity, water permeability resistant, compressive strength and flexural strength performance in both air and water environment than control MPC mortar over the whole test protocol time. MPC composites bearing 15% BC revealed the density, porosity and water diffusion coefficient (WDC) around 2.45 g/cm(3) at 14 d, 2.65% at 14 d and 0.04 mm(2)/s at 8 h, respectively, and the uniaxial compressive and flexural strength showed around 82.7 MPa and 11.4 MPa at 28 d in air curing regime. Additionally, the microstructure analyzed by XRD and SEM also corroborated the strength performances and engineering parameters of specimens. Fourier Transform Infrared spectroscopy (FTIR) analysis also showed the absence of new chemical groups formation between the interaction of BC and MPC pastes, which proved that BC acted only as pore-filled material for improving the engineering properties. The findings of the current study might be a potential solution to produce the cost-effective BC-MPC block with durable quality. (C) 2019 Elsevier Ltd. All rights reserved.

Experimental research of water stability of magnesium alumina phosphate cements mortar

Experimental research on magnesium phosphate cements containing alumina

Effects of Alumina As an Effective Constituent of Metakaolin on Properties of Magnesium Phosphate Cements

Experimental Study of Magnesium Phosphate Cements Modified by Metakaolin

Effect of Metakaolin on the Water Resistance of Magnesium Phosphate Cement Mortar

Effects of Aluminum Silicate on Mechanical Strength and Microstructural Improvement of Magnesium Phosphate Cement Mortar

Chemical–physical–mechanical Stability of MKG Mortars under Sulfate Attacks

Water-resisting Performances and Mechanisms of Magnesium Phosphate Cement Mortars Comprising with Fly-Ash and Silica Fume

Thermodynamic modeling of magnesium ammonium phosphate cement and stability of its hydration products

Experimental Study of Phosphate Salts Influencing Properties of Magnesium Phosphate Cement

Hydration properties of magnesium phosphate cement paste mixed with metakaolin and silica fume

Investigations on phase constitution, mechanical properties and hydration kinetics of aluminous cements containing magnesium aluminate spinel

Study on the hydration process and borax retarding mechanism of the magnesium ammonium phosphate cement-based coating system

Study on Performance of Magnesium Phosphate Cement

The Role of Bauxite and Fly-Ash on the Water Stability and Microstructural Densification of Magnesium Phosphate Cement Composites

Experimental Research on Properties and Microstructures of Magnesium-Iron Phosphate Cement

Experimental research on magnesium phosphate cement mortar reinforced by glass fiber

Engineering Properties and Microstructure Analysis of Magnesium Phosphate Cement Mortar Containing Bentonite Clay

Effects of Bauxite Tailings and Sodium Silicate on Mechanical Properties and Hydration Mechanism of Magnesium Phosphate Cement

Study on flexural resistance and hydration mechanism of magnesium phosphate cement

Mechanical Properties and Hardening Mechanism of Magnesium Ammonium Phosphate Cements Modified by Fly Ash