Abstract:The ability to synthesizing monodisperse Li4Ti5O12 (LTO) nanospheres is the key to reducing the irreversible capacity of LTO materials, and thus improving their power performance. However, it remains a grand challenge to achieve uniform precursors of LTO nanospheres and maintain their spherical structures after annealing. Herein, we develop a robust strategy for the synthesis of monodisperse LTO nanospheres with an average diameter of 120nm via the use of titanium nitride (TiN) as a titanium source for lithium ion batteries (LIBs). The precursors composed of uniform TiO2/Li+ nanospheres were formed in a stable alkaline environment during the course of heating of the solution of peroxo-titanium complex as a result of the dissolution of TiN, while TiO2/Li+ microspheres were easily yielded with the decrease in pH value of the precursor solution. The OH− anion was found to effectively retard the hydrolysis of peroxo-titanium complex as well as the aggregation of TiO2/Li+ nanoparticles. Intriguingly, a uniform polyvinyl pyrrolidone (PVP) layer formed in-situ on the surface of TiO2/Li+ nanospheres rendered LTO to retain the monodisperse spherical morphology after annealing. Notably, the as-prepared monodisperse LTO nanospheres comprised of the interconnected LTO nanograins with an average size of ~15nm uniformly coated by a carbon layer derived from the carbonization of PVP exhibited a high tap density (1.1gcm−3) and an outstanding rate-cycling capability. The charge specific capacities at 1, 10, 50 and 80C were 159.5, 151.1, 128.8 and 108.9mAh g−1, respectively. More importantly, the capacity retention after 500 cycles at 10C was as high as 92.6%. This work opens up an avenue to craft the uniform precursors of LTO and thus monodisperse LTO nanospheres that possess superior rate performance with high volumetric energy densities and long-term cyclic stability.

Synthesis of quasi-spherical micro-size lithium titanium oxide by an easy sol-gel method

Monodispersed mesoporous Li4Ti5O12 submicrospheres as anode materials for lithium-ion batteries: morphology and electrochemical performances.

Synthesis and assessment of the electrochemical performance of micro-nano-spherical Li4Ti5O12-LiAlO2 composites

High Performance Ti3+ Self-Doped Li4Ti5O12 Anode Materials Synthesized by an Electrochemical Method in Molten Salt

Synthesis of Monodisperse Mesoporous TiO2 Nanospheres from a Simple Double-Surfactant Assembly-Directed Method for Lithium Storage.

Mesoporous Spherical Li₄Ti₅O₁₂ As High-Performance Anodes for Lithium-Ion Batteries.

Mesoporous Spherical Li<sub>4</sub>Ti<sub>5</sub>O<sub>12</sub> as High‐Performance Anodes for Lithium‐Ion Batteries

Synthesis of dual-modified Fe-doped and carbon-coated Li4Ti5O12 anode based on industrial H2TiO3 for Li-ion batteries

Cost-effective Li4Ti5O12/C–S prepared by industrial H2TiO3 under a carbon reducing atmosphere as a superior anode for Li-ion batteries

Micelle-directed Self-Assembly of Single-Crystal-like Mesoporous Stoichiometric Oxides for High-Performance Lithium Storage.

Solvothermal Synthesis and the Electrochemical Property of Nano-sized TiO2 Anode Materials for Lithium-ion Batteries

Oxygen Vacancy-Modulated Zeolitic Li4ti5o12 Microsphere Anode for Superior Lithium-Ion Battery

A Robust Strategy for Crafting Monodisperse Li4Ti5O12 Nanospheres As Superior Rate Anode for Lithium Ion Batteries

Hydrothermal Synthesis of Li4Ti5O12/TiO2 Nano-composite As High Performance Anode Material for Li-Ion Batteries

Fabrication of hollow TiO2 nanospheres for high-capacity and long-life lithium storage

Facile Synthesis of Hierarchically Porous Li4Ti5O12 Microspheres for High Rate Lithium Ion Batteries

Li2TiSiO5: a low potential and large capacity Ti-based anode material for Li-ion batteries

Flower-like TiO2 hollow microspheres with mixed-phases for high-pseudocapacitive lithium storage

Synthesis of Mesoporous Lithium Titanate Thin Films and Monoliths as an Anode Material for High-Rate Lithium-Ion Batteries

Facile Synthesis of Pre-Lithiated LiTiO<sub>2</sub> Nanoparticles for Quick Charge and Long Lifespan Anode in Lithium-Ion Batteries

Li4Ti5O12 Prepared by a Modified Citric Acid Sol–gel Method for Lithium-Ion Battery