Abstract:Nanostructured zinc oxide (ZnO) for gas sensing application has been prepared by using normal and oblique angle sputtering deposition techniques under different substrate temperatures. Oblique angle plasma beam deposition is demonstrated effectively growing large-area uniformly aligned and inclined ZnO nanorod arrays on catalyst-free silicon substrate due to a self-shadowing mechanism, whereas normal radio frequency sputtering deposition yields nanoparticles as island growth mode. Furthermore, the density of the nanorod arrays is dependent on the incident angle of ZnO plasma beam. With an increase of the incident flux angle, large inter spacing was induced, resulting in sparser nanorod arrays. The nanorod arrays grown with an incident angle of 70 have an average diameter of similar to 150-300 nm and length of similar to 700-750 nm. The experimental data from characterization of the samples indicates that the obtained samples at different substrate temperatures and incident angles have wurtzite structure with a c-axis orientation.Sensing characterization reveals that the nanorod-based sensor shows higher sensitivity, faster response and recovery time, as well as better reproducibility than that of nanoparticle-based gas sensor to 100 ppm hydrogen and methane at low operating temperature below 150 degrees C due to the porosity and large grain boundaries of the nanorod arrays. It demonstrates that oblique angle of sputtering deposition is a simple, inexpensive synthesis process to get high-porosity nanostructures and as a result, improves the sensing properties of fabricated ZnO sensors, which permits us to obtain sensors with high sensitivity, low operating temperature and stability. (C) 2011 Elsevier B.V. All rights reserved.

Facile fabrication and enhanced gas sensing properties of the ultrathin ZnO nanoplates

Fabrication and Gas‐Sensing Properties of Porous ZnO Nanoplates

Enhanced performance of the tangerines-like CuO-based gas sensor using ZnO nanowire arrays

Hydrothermal Synthesis of Ultrathin ZnO Nanosheets and Their Gas-Sensing Properties

Fabrication of Au Decorated Porous ZnO Microspheres with Enhanced Gas Sensing Properties

Porous and Single-Crystalline ZnO Nanobelts: Fabrication with Annealing Precursor Nanobelts, and Gas-Sensing and Optoelectronic Performance

Nanostructures and Sensing Properties of ZnO Prepared Using Normal and Oblique Angle Deposition Techniques

Porous ZnO Nanosheets:Fabrication and Gas-sensing Properties

Au-deposited Porous Single-Crystalline ZnO Nanoplates for Gas Sensing Detection of Total Volatile Organic Compounds

Room-temperature solid state synthesis of ZnO/α-Fe2O3 hierarchical nanostructures and their enhanced gas-sensing properties

Synthesis ofporous single-crystalline ZnO nanoplates and their sensing properties to indoor air pollutants

Fabrication of ZnO Nanoparticles Modified by Uniformly Dispersed Ag Nanoparticles: Enhancement of Gas Sensing Performance

Enhancing gas-sensing property and sensing mechanism at molecule level of the hollow microspheres assembled with ZnO nanoflakes exposing {001} facets

Self-assembly of ZnO Nanosheets into Flower-Like Architectures and Their Gas Sensing Properties

Fabrication of Spindle-Like ZnO Architectures for Highly Sensitive Gas Sensors

Large-scale Syntheses of Uniform ZnO Nanorods and Ethanol Gas Sensors Application

One-Dimensional Zinc Oxide Decorated Cobalt Oxide Nanospheres for Enhanced Gas-Sensing Properties

Enhanced Ethanol Sensing Properties of Ultrathin ZnO Nanosheets Decorated with CuO Nanoparticles

High-performance photodetectors, photocatalysts, and gas sensors based on polyol reflux synthesized porous ZnO nanosheets

Synthesis of ZnO nanosheet arrays with exposed (100) facets for gas sensing applications.

Synthesis of hierarchical ZnO nanostructure assembled by nanorods and their performance for gas sensing