Abstract:In this article, we fabricated ZnO nanorod arrays on ITO substrates by cathodic electrodeposition method under different electrodeposition times. The XRD results illustrate that all of the peaks can be attributed to the hexagonal wurtzite structure. Besides, the crystallinity and the preferred c-axis orientation increase with longer electrodeposition time. With the increasing electrodeposition time, the diameter of nanorods, the surface roughness and thickness of ZnO nanorod arrays also increased. All samples exhibit hydrophobic behavior and the water contact angle (CA) increases to 120 degrees with the electrodeposition time increases to 120 min. After 10 min of ultraviolet (UV) irradiation, the wettability of the ZnO surfaces turn from hydrophobic to hydrophilicity, and the change of the CA reduction rate are 73.5, 63.5, 48.3 and 24.2%, corresponding to the sample electrodeposited 10, 30, 60 and 120 min, respectively. The intensity of UV emission peak ratio increases from 2.26 to 63.84% while the visible emission peak ratio decreases in PL spectra, which reveals defects decrease when electrodeposition time increases from 10 to 120 min. Raman spectrum shows three peaks which are located at 439, 566 and 1097 cm(-1), corresponding to the E-2, E-1L and E-3 mode of ZnO. (C) 2016 The Electrochemical Society. All rights reserved.

Ordered ZnO nano-rod array films prepared by low cost electrochemical deposition and its optical properties

A large-scale-oriented ZnO rod array grown on a glass substrate via an in situ deposition method and its photoconductivity

Effect of Electrodeposition Time on Microstructure, Wettability and Optical Properties of ZnO Nanorod Arrays

Conversion of large-scale oriented ZnO rod array into nanotube array under hydrothermal etching condition via one-step synthesis approach

Low-Temperature Synthesis and Optical Property of ZnO Nanorod Arrays

Growth of ZnO Microrod Array Films and Their Optical Properties

Preparation of ZnO Nanorod Arrays by Seed-assisted Chemical Bath Deposition Method

Zno Nanorod Arrays with Tunable Size and Field Emission Properties on an Ito Substrate Achieved by an Electrodeposition Method

Hydrothermal Synthesis of Well-Aligned ZnO Nanorod Arrays on Silicon

ZnO Nanorod Arrays: Field-assisted Growth in Aqueous Solution and Field Emission Properties

Synthesis of Monodispersed Zno Nanorod Array Films by Chemical Solution Deposition.

Controlled Growth of ZnO Array on FTO Glass Substrate by Electrodeposition

Fabrication and Optical Properties of Highly Ordered ZnO Nanodot Arrays

Synthesis and optical property research of well-ordered ZnO nanorods arrays based on Al_2O_3 membrane

Synthesis and Optical Properties of Well-Aligned ZnO Nanorod Array on an Undoped ZnO Film

A facile route to ZnO nanorod arrays using wet chemical method

Fabrication of oriented ZnO nanorod arrays and their optical performances

Synthesis of aligned ZnO submicron rod arrays by heating zinc foil covered with ZnCl2 solution

Aligned ZnO Nanorod Arrays Fabricated on Si Substrate by Solution Deposition

Synthesis of Nano/Micro Zinc Oxide Rods and Arrays by Thermal Evaporation Approach on Cylindrical Shape Substrate

Density-controlled Growth and Passivation of ZnO Nanorod Arrays by Electrodeposition