Abstract:Abstract Global warming is one of the most significant issues the world is facing. Capturing carbon dioxide from the atmosphere or industrial processes and storing it in geological formations (carbon capture and storage, CCS) can help counteract climate change. Nevertheless, the interaction between well barrier elements such as cement, casing, tubulars, packers, and valves can lead to possible leakages. To accomplish successful carbon dioxide sequestration, injecting the carbon dioxide in its supercritical state is necessary. The supercritical carbon dioxide can corrode steel and elastomers and react with the calcium compounds in the cement, dissolving them and forming calcium carbonate and bicarbonate in the process. This carbonation can lead to channels forming on the cement-to-rock interface or cracking due to the carbonate precipitation, resulting in a loss of well integrity. This study focusses on finding ways that enable the continuous monitoring of cement integrity, under in-situ conditions, in a lab setup. The construction of an autoclave, capable of withstanding supercritical conditions of carbon dioxide, facilitates the in-situ monitoring. This autoclave also makes CT-scans of the pressurized sample possible, as well as acoustic measurements, using state-of-the-art piezo elements. The first tests will establish a baseline using neat Class G Portland cement to verify the design and sensors. The set up consists of a rock core in the middle of the autoclave surrounded by a cement sheath. A prepared channel in the center of the core expedites the distribution of the carbon dioxide. Once the ability of the sensors to monitor the integrity is verified, different cement compositions and their interaction with supercritical carbon dioxide can be studied. The experimental setup and the procedure discussed here closely simulate the downhole condition. Hence, the results obtained using this setup and procedure is representative of what could be observed downhole. The direction is not to remove the sample from the autoclave for analysis, as is the current industry practice, but to measure cement integrity under in-situ conditions over an extended period of time. Digitalization is powering the in-situ analysis in these tests. The first two tests of this study, using the afore mentioned autoclave, investigated the carbonation behaviour of two Class G Portland cement slurrys, one with a low and one with a high slurry-density. The low-density slurry showed extensive degradation and even the high-density slurry showed carbonation, but only close to the sandstone core. The results from this study can lead to the prevention of leakage of carbon dioxide to the environment and other formations, which defeats the purpose of carbon dioxide sequestration. These results should improve the economics of these wells as well as the health, safety, and environmental aspects.

Research on Carbon Dioxide Corrosion of Cement Stones of Oil Well Casings under High Temperature and High Pressure

Carbon Dioxide Corrosion and Corrosion Prevention of Oil Well Cement Paste Matrix in Deep Wells

Study on the Oil Well Cement-Based Composites to Prevent Corrosion by Carbon Dioxide and Hydrogen Sulfide at High Temperature

Study on the properties of nano silica modified cement for cementing

Degradation of chemical and mechanical properties of cements with different formulations in CO2-containing HTHP downhole environment

Corrosion Characteristics of Polymer-Modified Oil Well Cement-Based Composite Materials in Geological Environment Containing Carbon Dioxide

Effect of CO2 solution on Portland cement paste under flowing, migration, and static conditions

The Influence of CO2 Physical Properties on Casing and Its Prediction Method

A new method to protect the cementing sealing integrity of carbon dioxide geological storage well: An experiment and mechanism study

Enhancing the CO2-H2S corrosion resistance of oil well cement with a modified epoxy resin

Experimental Study on Corrosion of J55 Casing Steel and N80 Tubing Steel in High Pressure and High Temperature Solution Containing CO2 and NaCl

Research on Wellbore Integrity Evaluation Model of CO2 Enhanced Composite Fracturing

Real-Time Monitoring of the Effect of CO2 on the Cement Sheath

Corrosion integrity of oil cement modified by environment responsive microspheres for CO2 geologic sequestration wells

Study on multicomponent composite anti-corrosion cement slurry system suitable for ultra-high temperature acid gas wells

Well Cement Degradation and Wellbore Integrity in Geological CO2 Storages: A Literature Review

The Failure Mechanism and Countermeasures of Cement Sheath in Vertical Section of Well during Hydraulic Fracturing

Sealing Failure Mechanism and Control Method for Cement Sheath during Hydraulic Fracturing

Study on Failure Behavior of Gas Well Tubing Under CO 2 Corrosion After Erosion

Preparation of Nano-SiO2/Carbon Fiber-Reinforced Concrete and Its Influence on the Performance of Oil Well Cement

Thermodynamic analysis of the corrosion of high alumina cement by carbon dioxide