Abstract:Titanium carbide (TiC) particulates-reinforced iron matrix composites were prepared by in situ fabrication method combining an infiltration casting with a subsequent heat treatment. The effects of different heat treatment times (0, 1,6 and 11 h) at 1138 degrees C on the phase evolution, microstructural features, and properties of the composites were investigated. The as-prepared composites were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), and microhardness and wear resistance tests. The XRD results showed that the composites consisted of graphite, alpha-iron and titanium carbide after heat treatment at 1138 degrees C for 11 h. The SEM observation revealed that the formed TiC particulates were homogenously distributed in the iron matrix. The average microhardness of the composite heat treated at 1138 degrees C for 6 h increased depending upon the region: 209 HV0.1 (iron matrix) <787 HV0.1 (titanium wire) < 2667 HV0.1 (composite region). After being heat treated at 1138 degrees C for 11 h, the composite indicated no considerable change in microhardness value, and the average microhardness of the composite region was about 2354 HV0.1. The highest microhardness value obtained for the composite region was due to the formation of titanium carbide particulates as reinforcement phase within the iron matrix. Relative wear resistance was determined by a pin-on-disc wear test technique under different loads, and as a result, the composites containing higher volume fraction of hard titanium carbide particulates presented higher wear resistance compared with the unreinforced gray cast iron. (C) 2011 Elsevier Ltd. All rights reserved.

Microstructure and Wear Properties of In Situ Production of (Fe,Cr)7C3 Particulate Bundles Reinforced Iron Matrix Composites

Microstructure and Wear Properties of<i> In Situ </i>Production of (Fe,Cr)<sub>7</sub>C<sub>3</sub> Particulate Bundles Reinforced Iron Matrix Composites

In-Situ Production of (Fe,cr)(7)c-3 Particulate Bundles Reinforced Iron Matrix Composites

Research on Microstructure of In-situ Production of (Fe,Cr)7C3 Particulate Bundles Reinforced Iron Matrix Composite

Infiltration Casting and <i>In Situ</i> Fabrication of (Fe,Cr)<sub>7</sub>C<sub>3</sub> Particulates Bundle – Reinforced Iron Matrix Composites

Infiltration casting and in-situ fabrication of (Fe,Cr) 7C 3 particulates bundle - Reinforced iron matrix composites

Microstructure and Wear Resistance of Iron Matrix Composites Reinforced by In-Situ Carbides

In Situ NbC Particulate-Reinforced Iron Matrix Composite: Microstructure and Abrasive Wear Characteristics

In Situ Fabrication of Titanium Carbide Particulates-Reinforced Iron Matrix Composites

Investigation on Microstructure and Mechanism of In-situ Producing Grey Cast Iron Matrix Composite

Microstructure, Microhardness and Wear Resistance of VCp/Fe Surface Composites Fabricated in Situ

Fabrication and microstructure of in situ vanadium carbide ceramic particulates-reinforced iron matrix composites

(Fe, Cr)7C3/Fe Composite In-situ Synthesized by Cast Iron and Cr Bar

Microstructure and Dry Sliding Wear Behavior of Fe-Based (Cr, Fe) 7 C 3 Composite Coating Fabricated by PTA Welding Process

Infiltration Casting and in Situ Fabrication of NbC Particulates – Reinforced Iron Matrix Composites

Interfacial bonding and wear behavior of macroscopic TiC particulates reinforced iron-based composites fabricated by infiltration casting process

Abrasive wear properties of titanium carbide particle bundle reinforced iron matrix composite prepared by in-situ synthesis

Abrasive wear characteristics of in-situ TiC-reinforced iron matrix surface gradient composites

Interface and wear characteristics of high-Cr cast iron matrix composite reinforced with cemented carbide particles

Friction and Wear Performance of Carbide (cr, Fe)7C3-reinforced Fe-based Composite Coating

Interface Structure and Wear Behavior of Cr26 Ferrous Matrix Surface Composites Reinforced with CTC P