Abstract:Nano-ZSM-5 with large amount and high strength of acid sites were successfully synthesized by hydrothermal crystallization of pure-silica nucleus in NaAlO2 alkali solution. The concentration of NaAlO2 alkali solution was decreased by increasing the H2O/Al ratio from 200 to 2600, which strongly determined the acidic properties and crystal size of the obtained nano-ZSM-5. Low concentration of NaAlO2 alkali solution was found unfavorable for the incorporation of Al into the bulk of ZSM-5 crystal in crystallization process. Hence, more Al distributed at the exterior of crystals, which enhanced the accessibility of the acid sites during reaction. Large amount and high strength of acid sites were produced for nano-ZSM-5 by increasing H2O/Al ratio. When the H2O/Al ratio increased from 200 to 2600, the total amount of acid sites increased from 0.59 to 0.81 mmol g(-1), much higher than conventional value of 0.50 mmol g(-1). In addition, the acid strength increased and the ratio of Bronsted/Lewis acid sites were sharply increased from 2.3 to 4.1 when the H2O/Al ratio increased. Moreover, the size of nano-crystal was also decreased by above decreasing the concentration of the NaAlO2 alkali solution. When the H2O/Al ratio was 2600, the obtained sample possessed total acid amount of 0.81 mmol g(-1) and crystal size of 60 nm, respectively. Methanol to hydrocarbon (MTH) reaction results showed that the increased acid sites of the catalyst decreased its catalytic lifetime to some extent, but the aromatics selectivity was tunable obviously. As for the catalyst prepared with H2O/Al ratio of 2000, the aromatics selectivity of the obtained catalyst reached to 66.0%. This paper provided a method for the fabrication of small-size nano-ZSM-5 with large amount and high strength of acid sites and regulated Al distribution for MTH reaction.

Synthesis of Methylal from Methanol and Trioxane over Acidic Resin

Influence of Acid-Base Properties of ZnMgAl-mixed Oxides for the Synthesis of 1-Methoxy-2-propanol

An Insight into Effect of Methanol on Catalytic Behavior of Amberlyst 35 Resins for Alkylation Desulfurization of Fluid Catalytic Cracking Gasoline

An atom-economic reaction for synthesis of 1-phenoxy-2-propanol over Al2O3/MgO

Zirconium-Modified Cs/SiO2 Catalyst for Synthesis of Methyl Acrylate Via Aldol Condensation of Methyl Acetate with Formaldehyde

Synthesis of methylal from methanol and formaldehyde catalyzed by Brønsted acid ionic liquids with different alkyl groups

Effect of Methanol on Catalytic Performance of Hy Zeolite for Desulfurization of Fcc Gasoline by Alkylation

SOLID-ACID CATALYSTS FOR VAPOR PHASE DEHYDRATION OF METHANOL TO DIMETHYL ETHER

One-step Aldol Condensation Reaction of Dimethoxymethane and Methyl Acetate over Supported Cs/ZSM-35 Zeolite Catalysts

A Green Route to Methyl Acrylate and Acrylic Acid by an Aldol Condensation Reaction over H-ZSM-35 Zeolite Catalysts

Study on the Synthesis of Polyoxymethylene Dimethyl Ethers

Synthesis of Polyoxymethylene Dimethyl Ethers Catalyzed by Brønsted Acid Ionic Liquids with Alkanesulfonic Acid Groups

Catalytic Synergy Between the Low Si/Al Ratio Zn/ZSM-5 and High Si/Al Ratio HZSM-5 for High-Performance Methanol Conversion to Aromatics

Reaction Kinetics of Methanol Dehydration over Combined AI203-HZSM-5 Solid Acids

Formation of Methyl Acrylate from Methyl Acetate and Formaldehyde Condensation over Solid Base Catalysts

Clean Synthesis of Acetaldehyde Oxime Through Ammoximation on Titanosilicate Catalysts

Synthetic Technics of Methyl Acrylate Through Aldol Condensation with a Multisubsection Fixed-Bed Reactor

Controllable Synthesis of Nano-Zsm-5 Catalysts with Large Amount and High Strength of Acid Sites for Conversion of Methanol to Hydrocarbons

Performance and Characterization of Supported Rhenium Oxide Catalysts for Selective Oxidation of Methanol to Methylal

Effect of Alkaline Concentration on Mesopore Formation in Acid Pre-treated HZSM-5 Zeolite and Its Catalytic Performance in the Methanol-to-Gasoline Reaction

Alkylation for Removing Trace Olefins from Reforming Aromatics over Novel Al2O3@SO42-/ZrO2 Catalysts Derived from the ZrO2-coated Γ-Al2o3 Strategy