Application of Copper for Sufficient Metal Extraction from Zinc Leaching Residue: Process Optimization and Copper Reuse
Limin Zhang,Yunyan Wang,Yun Li,Zhumei Sun,Yong Ke,Cong Peng,Mingfei Zhu,Yongjian Luo,Xiaobo Min
DOI: https://doi.org/10.1016/j.mineng.2024.108763
IF: 5.479
2024-01-01
Minerals Engineering
Abstract:The advanced treatment of zinc leaching residue (ZLR) is of significance for carbon reduction and sustainable development of zinc smelting industry. Herein, a fast and sufficient hydrometallurgical extraction of metals from zinc leaching residue under mild conditions was proposed via application of metal copper. The results showed that 85.07 % Cu, 97.20 % Cd, 95.05 % As, 96.65 % Mn, 95.86 % In, and 96.81 % Co in ZLR were leached, with Pb and Ag enriched in the residue by over 4 times. Copper powder in the leaching solution enhanced the acid dissolution of zinc ferrite in ZLR. More than 90 % of zinc was extracted within 15 min at 80 degrees C, 20 min at 70 degrees C, or 40 min at 60 degrees C under the optimal leaching conditions: n(Cu)/n(ZnFe2O4) = 1, 500 g/L H2SO4, and 4 mL/g. In addition, copper cemented by zinc powder was reused in the leaching process of ZLR and showed good performance. The proposed copper-assisted leaching process of ZLR was advanced in productivity, the metal recycling rate, and facilities. This study provided an alternative for the treatment of ZLR without use of coal, hopefully contributing to the carbon reduction in zinc smelters.