Experimental Analysis of Influence of Iron Tailings Sand on Mechanical Properties of Shotcrete
Zhengjun HUANG,Ying ZHANG,Fenhua REN,Lei ZHANG,Qifeng GUO
DOI: https://doi.org/10.13827/j.cnki.kyyk.2019.04.026
2019-01-01
Abstract:In order to study the mechanical properties of iron tailings instead of natural sand, a total of 14 tests were designed for 6 mixing schemes.The slump test, initial setting time test, block density test, compressive strength test, and splitting tensile strength test were carried out separately, and scanning electron microscopy analysis was carried out on the specimens with different mixing proportions under concrete pouring and curing for 28 days.The results showed that the iron tailings sand was added to concrete as fine aggregate, when the ratio of iron tailings sand to the total fine aggregate (the sum of iron tailings sand and natural sand) was 20％, the workability and coagulation time were optimal, the block density was the largest, and the durability was the best.But when the ratio exceeded 20％, the workability and durability gradually decreased.The scanning electron microscopy results confirmed the mechanical strength variation of concrete.The optimum water-cement ratio, limesand ratio and admixture content were obtained at the 8 th mix ratio scheme, and the compressive strength of the concrete at the second mix ratio scheme was the greatest.The compressive strength and tensile strength of the concrete at the second scheme were the highest in 1, 3 and 7 days, and the tensile strength of the concrete at the second scheme was similar in 7 days and 28 days, which met the optimum requirement of shotcrete performance.The experimental results showed that the performance characteristics of shotcrete could be effectively improved by using iron tailings in the preparation of shotcrete, of which the second scheme was the best.