Abstract:Rare earth aluminate phosphors are well-known for being nontoxic and environmentally friendly. In this work, Tb3+-doped SrLaAlO4 phosphors were synthesized via a facile high temperature solid-state reaction method. The Optimum reaction temperature is determined to be 1300 degrees C based on the results of powder X-ray diffraction (XRD). The SEM patterns and TEM images correspond with the results of Rietveld refinement and show that the SrLa1-xAlO4:xTb(3+) samples present a flaky structure. The results of photoluminescence spectrums (PL) show that SrLa1-xAlO4:xTb(3+) phosphors can absorb in the UV-vis spectral region of 228 nm-263 nm and exhibit several emission peaks between 450 and 650 run, and the highest peak was at 508 nm. The luminescence properties of SrLa1-xAlO4:xTb(3+) have a strict dependence on the cation substitution levels. When the doping concentration of Tb3+ was 0.05, the emission intensity of the sample is strongest. The thermal quenching result of the SrLa0.95AlO4:xTb(3+) phosphors shows that these phosphors are relatively sensitive to temperature changes under an excitation of 228 nm, as the temperature increases from 25 degrees C to 125 degrees C, the emission intensity (peak at 548 nm) decayed to 55.11% of that at room temperature. However, when the temperature increases to 125 degrees C, the emission intensity (peak at 548 nm) decayed to 61.16% of the initial value under an excitation of 263 nm, which showed a relatively good thermal stability. The internal quantum efficiency (QE) values of the SrLa0.95AlO4:xTb(3+) phosphors was measured and determined to be 48%. Under excitations of 228 nm and 263 nm, the lifetimes of the optimized sample SrLa0.95AlO4:xTb(3+) were 1.3986 ms and 1.2095 ms, respectively, and the CIE coordinates of the sample were calculated as (0.2971, 0.4981), (0.3056, 0.5329), respectively. Under both excitations SrLa0.95AlO4:xTb(3+) exhibited high-color-purity green emission.

Facile Synthesis of LnPO4: Tb (ln = Ce, Gd) Green Emission Phosphors at Specific Temperature (80 or 680°С)

Thermally Stable Gd4(P2O7)3: Tb3+ Phosphor Synthesized Via Co-Precipitation: a Study on Ph-Dependent Formation and Luminescence

Preparation and Photoluminescence of the Ce-, Tb- and Gd-doped Lanthanum Borophosphate Phosphor

Electrodeposition of high aspect ratio LaPO 4 and LaPO 4 :Ln 3+ (Ln 3 + =Ce 3+ , Tb 3+ ) nanostructures

Hydrothermal Synthesis and Luminescent Properties of LnPO4:Tb (ln = La, Gd) Phosphors under VUV Excitation

Facile synthesis of Gd2O2SO4:Tb and Gd2O2S:Tb green phosphor nanopowders of unimodal size distribution and photoluminescence

Simple Preparation of LaPO4:Ce, Tb Phosphors by an Ionic-Liquid-Driven Supported Liquid Membrane System

Structure, Photoluminescence and Influence of Temperature on Energy Transfer of Green-Emission Phosphor Ca9La(GeO4)0.75(PO4)6:Ce3+,Tb3+

Synthesis of Hexagonal Prism (la, Ce, Tb)PO4 Phosphors by Precipitation Method

FACILE SYNTHESIS AND LUMINESCENE PROPERTIES OF CePO4:Tb3+ BY ELECTROSPINNING

Structure , Photoluminescence and Influence of Temperature in Energy Transfer in Green-emission Phosphor Ca 9 La ( GeO 4 ) 0 . 75 ( PO 4 ) 6 : Ce 3 + , Tb 3 +

Preparation and Luminescence Properties of Color-Tunable Single-Phased LaPO4:Eu3+/Tb3+ Phosphors

Facile Composite Synthesis and Photoluminescence of NaGd(MoO4)2: Ln3+(Ln = Eu, Tb) Submicrometer Phosphors

Green-Emitting Gd3Ga5O12: Tb3+ Nanoparticles Phosphor: Synthesis, Structure, and Luminescence

Preparation, Structure, Luminescence Properties of Terbium Doped Perovskite-Like Structure Green-Emitting Phosphors SrLaAlO4:Tb3+

Systematic synthesis of (Gd1‐xLax)2O2SO4:Tb3+ and (Gd1‐xLax)2O2S:Tb3+ nanophosphors for remarkably enhanced luminescence

Controlled Synthesis of Tb3+/Eu3+ Co-Doped Gd2O3 Phosphors with Enhanced Red Emission

Preparation of LaPO4:Ce,Tb phosphor with different morphologies and their fluorescence properties

Controlled Synthesis of Tb/Eu Co-Doped Gd₂O₃ Phosphors with Enhanced Red Emission.

Preparation and UVU Photoluminescence of Ce~(3+),Tb~(3+) Activated Lanthanum Borophosphate Phosphor

A Novel Green Phosphor GdCaAlO4:Tb3+ for PDP Application