Abstract:Concrete in structures is possibly exposed to fire and blast due to occasional accidents or terrorist attack during the service life. Yet, there are few experimental studies on the responses of normal concrete structures subjected to high temperature and high strain rate loading simultaneously, although some high strain rate experiments were performed before or after fire exposure. This paper reports an experimental study of the combined effects of high temperature and high strain rate on normal concrete material, which is a preliminary basis for calculating and assessing the performances of RC structures in blast and fire. The dynamic properties of normal concrete at elevated temperature from 20 °C up to 950 °C were systematically studied using a specially manufactured microwave–heating automatic time-controlled Split Hopkinson Pressure Bar (MATSHPB) apparatus. The concrete specimens were first efficiently heated in a specially designed industrial microwave oven, and then rapidly loaded after quickly rolling to the SHPB system. Quasi–static and low strain rate tests at elevated temperatures were also carried out for comparative analysis. In contrast with previous experimental research, the test results showed that the dynamic strength and stress–strain curve of normal concrete at high temperature still experienced remarkable strain rate effects. Moreover, the failure appearances of normal concrete subjected to both high temperature and high strain rate loading were significantly different from those of concrete at ambient temperature. In contrast with quasi-static test data, a new empirical model on dynamic increase factor of strength and secant elastic modulus of concrete at elevated temperature (DIFTS, DIFTE) were established that can be used in a very wide range of application.

Effects of Temperature and Strain-Rate on the Compressive Strength of Concrete

Experimental study on dynamic behavior of concrete at elevated temperatures

Strength of Concrete Filled Steel Tubes under High-Strain Rate Loading

Effect of High Temperature Exposure and Strain Rate on Mechanical Properties of High-Strength Steel Rebars

Experimental Studies on Concrete Filled Steel Tubes under High Strain Rate Loading

High-strain Rate Compressive Behavior of CFRP Confined Concrete: Large Diameter SHPB Tests

Strain-Rate Sensitivity of Concrete: Influence of Temperature

EXPERIMENTAL RESEARCH ON IMPACT BEHAVIOR OF CONCRETE-FILLED STEEL TUBE AT ELEVATED TEMPERATURES

Compressive Impact Tests of Lightweight Concrete with 155-Mm-diameter Spilt Hopkinson Pressure Bar

Coupled Effects of High Temperature and Strain Rate on Compressive Properties of Hybrid Fiber UHTCC

Dynamic Tensile Properties and Energy Dissipation of High-Strength Concrete after Exposure to Elevated Temperatures

Effect of Temperature on Pore Structure and Strength of Concrete

Effect of Elevated Temperatures on Compressive Strength of Concrete

Experimental investigation of the dynamic mechanical properties of concrete under different strain rates and cyclic loading

Comparative analysis of dynamic mechanical properties of steel fiber reinforced concrete under ambient temperature and after exposure to high temperatures

The effects of high temperature on compressive and flexural strengths of ordinary and high-performance concrete

Combined effects of high temperature and high strain rate on normal weight concrete

Experimental study on compressive strength of concrete under lasting sub-high temperature

Strain-rate sensitivity of concrete: Influence of moisture content

EFFECT OF STRAIN RATE ON THE BIAXIAL COMPRESSIVE BEHAVIOR OF CONCRETE

Comparison between high strength concrete and normal strength concrete subjected to high temperature