Enhancement of the Compatibility, Mechanical Properties, and Heat Resistance of Poly(butylene Succinate-Co-terephthalate)/poly(butylene Succinate) Blends by the Addition of Chain Extender and Nucleating Agent
Yan Xiangyu,Chen Ling,Tian Hanlin,Jia Shiling,Wang Xiangyu,Pan Hongwei,Han Lijing,Bian Junjia,Yang Huili,Wu Guangfeng,Zhao Yan,Zhang Huiliang
DOI: https://doi.org/10.1007/s10965-023-03486-z
IF: 3.061
2023-01-01
Journal of Polymer Research
Abstract:Poly(butylene succinate-co-terephthalate) (PBST) is an aliphatic–aromatic copolymer with excellent biodegradability and high flexibility, which can be used to replace traditional non-degradable polymer materials in various fields. However, its relatively low heat distortion temperature limits its applicability. Herein, poly(butylene succinate) (PBS) was blended with PBST to enhance the heat resistance of PBST. The chain extender ADR-4370F was used as a reactive compatibilizer to improve the compatibility between PBST and PBS. The hydrazide compound TMC-300 was use as a nucleating agent to improve the PBST/PBS blend's crystallization behavior and prepare a novel and eco-friendly PBST/PBS-based blend. The morphology of the cryo-fractured surfaces of PBST/PBS blends showed that the compatibility between PBST and PBS improved significantly upon adding ADR. Furthermore, compared to the PBST/PBS blend, Young's modulus, tensile strength, breaking strain, and breaking energy of the PBST/PBS/ADR blend showed great improvement. In addition, DSC results showed that the crystallization temperature ( T c ) of PBST and PBS of PBST/PBS/ADR/TMC blend increased with increasing TMC content. WAXD results showed that the degree of crystallinity of PBST/PBS/ADR/TMC blends increased with incorporating PBS and TMC, increasing the Vicat softening temperature. Compared with neat PBST, the heat resistance of the PBST/PBS-based blend was improved.