Abstract:Numerous studies have demonstrated that under low-velocity, low-energy impact conditions, although the surface damage to fiber-reinforced composite laminates may be minimal, significant internal damage can occur. Consequently, a progressive damage finite element model was specifically developed for thermoplastic carbon fiber-reinforced composite laminates subjected to low-speed impact loads, with the objective of analyzing the damage behavior of laminates under impacts of varying energy levels. The model utilizes a three-dimensional Hashin criterion for predicting intralayer damage initiation, with cohesive elements based on bilinear traction-separation law for predicting interlaminar delamination initiation, and incorporates a damage constitutive model based on equivalent displacement to characterize fiber damage evolution, along with the B-K criterion for interlaminar damage evolution. The impact response of laminates at energy levels of 5 J, 10 J, 15 J, 20 J, and 25 J was analyzed through numerical simulation, drop-hammer experiments, and XCT non-destructive testing. The results indicated that the simulation outcomes closely correspond with the experimental findings, with both the predicted peak error and absorbed energy error maintained within a 5% margin, and the trends of the mechanical response curves aligning closely with the experimental data. The damage patterns predicted by the numerical simulations were consistent with the results obtained from XCT scans. The study additionally revealed that the impact damage of the laminates primarily stems from interlaminar delamination and intralayer tensile failure. Initial damage typically presents as internal delamination; hence, enhancing interlaminar bonding performance can significantly augment the overall load-bearing capacity of the laminate.

Experimental Research on CFRP Laminates with Different Impact Energy Levels

Experimental Research on the Impact Damage of Composite Laminates at Different Energies

Experimental research on the effects of dimension on the impact damage of CFRP laminates

Experimental Research on Medium Leakage of CFRP Laminates after Impact

The Impact Damage and Medium Leakage of Cfrp Laminates with Different Thickness

Low-velocity impact behavior and residual tensile strength of CFRP laminates

Threshold Of Impact Energy On The Medium Leakage Of Cfrp Laminates

Experimental Investigation of the Double Impact Position Effect on the Mechanical Behavior of Low-Velocity Impact in CFRP Laminates

Impact responses and residual flexural properties of narrow CFRP laminates

Experiments of impact damage of CFRP laminates with voids

Changes in Dynamic Mechanical Behavior of Carbon Fiber Reinforced Polymer Laminates under Multiple Low Energy Impacts

Research on the Damage Assessment of Carbon/Epoxy Composite Laminates at Different Impact Energy

Low-velocity Impact Damage Research on CFRPs with Kevlar-fiber Toughening

Low-Velocity Impact Behavior and Damage Characteristics of CFRP Laminates

Residual bending strength after impact of CFRP laminates in hygrothermal condition

Experimental Characterization of the Mechanical Strength after Impact of CFRP Laminates with Different Void Contents

Exploration of Energy Absorption and Viscoelastic Behavior of CFRPs Subjected to Low Velocity Impact

Research on impact damage of CFRP laminates with different void contents

Experimental Study of Dynamic Mechanical Properties of Composite Laminate Plate under the Impact Loading

Experimental and Simulation Study on Failure of Thermoplastic Carbon Fiber Composite Laminates under Low-Velocity Impact

Energy Absorption Efficiency of Carbon Fiber Reinforced Polymer Laminates under High Velocity Impact