Abstract:In this paper, metal inert gas (MIG) welding of 6082-T6 aluminum alloy with a thickness of 4 mm was simulated using a double ellipsoidal heat source. Based on the simulation results, the evolution of the microstructure, the strengthening mechanism of mechanical properties, and the corrosion characteristics of the welded joint were studied further. The thermal cycle curve of the welded joint was obtained through numerical simulation. When the heat input was 2.34–2.75 KJ/mm, the temperature of the welded joint reached the melting point of the material. With the increase in welding heat input, the weld metal (WM) organization changed from the dendrite to the cellular crystal transformation and presented a uniform distribution. The precipitation of the strengthened phase was inhibited at 2.75 KJ/mm. When the heat input changed from small to large, the tensile strength and toughness first increased and then weakened. Dimple distribution of tensile fractures was observed with a scanning electron microscope. When the welding heat input was 2.57 KJ/mm, the mechanical properties of the joint were the best. The tensile strength can reach 76.62% of the base material, and the elongation after breaking can reach 59.38% of the base material. However, it was concluded through studying electrochemical corrosion that the corrosion resistance of welded joints under this parameter was the worst. This may be caused by the presence of Cu, Fe, Si, Mg, and other compounds, and was proven to be Mg2Si through EDS analysis.

Microstructure and Mechanical Properties of Aluminum/Stainless Steel Joints Welded by Different Weld Heat Input

Interfacial Microstructure and Mechanical Properties of Aluminium-Zinc-Coated Steel Joints Made by A Modified Metal Inert Gas Welding-Brazing Process

Effect of Heat Input on the Microstructure and Mechanical Properties of 6060 Aluminum Alloy/Galvanized STEEL MIG Welding–Brazing Joints

Comparison of Microstructure and Mechanical Properties of TIG and Laser Welding Joints of a New Al–Zn–Mg–Cu Alloy

Microstructures and Mechanical Behavior of Aluminum-Copper Lap Joints

Interface Microstructure and Mechanical Property of CMT Welding-Brazed Joint Between Aluminum and Galvanized Steel Sheet

Effect of the Microstructure of IMCs and Zinc Accumulation on the Mechanical Properties of Aluminum/galvanized Steel Joints in the VP-CMT Process

Determination and Characterization of Heat Input, Microstructure and Performance in Cold Metal Transfer Weld-Brazing of Dissimilar AA6061-T6 to SS304 Sheets

Effect of Heat Input on Microstructure and Mechanical Properties of Ti/Cu66V34/Cu Joints by Electron Beam Welding

Microstructure and Mechanical Performance of Cold Metal Transfer Spot Joints of AA6061-T6 to Galvanized DP590 Using Edge Plug Welding Mode

Microstructure and Mechanical Performance of Dissimilar Metal Joints of Aluminium Alloy and Stainless Steel by Cutting-Assisted Welding-Brazing

Study of Microstructure and Fatigue in Aluminum/Steel Butt Joints Made by CMT Fusion-Brazing Technology

Interfacial Microstructure and Mechanical Properties of AZ31B/AA7075 Joints Using Non-Equilibrium Thermal Compensation Resistance Welding

Study on the Morphology, Microstructure, and Properties of 6082-T6 Aluminum Alloy Joints in MIG Welding

Microstructure and Mechanical Properties of Resistance-Spot-welded Joints for A5052 Aluminum Alloy and DP 600 Steel

Microstructure and Mechanical Properties of Pulsed Laser Welded Al/steel Dissimilar Joint

Microstructure and Properties of Dissimilar Butt Joints of Aluminum to Copper by Cold Metal Transfer with Preheating

Microstructure Characteristics and Properties of Mg/Al Dissimilar Metals Made by Cold Metal Transfer Welding with ER4043 Filler Metal

Effect of Heat Input on Microstructure and Mechanical Properties of Laser Welded Medium Mn Steel Joints

Weld Formation Mechanism and Microstructural Evolution of TC4/304 Stainless Steel Joint with Cu-Based Filler Wire and Preheating

Microstructural evolution and its effect on mechanical properties in different regions of 2219-C10S aluminum alloy TIG-welded joint