Abstract:This paper addresses the study of the complex effect of alloying elements (magnesium, manganese, copper and zirconium) on changes in magnesium-rich aluminum alloy composition, fine and coarse particle size and number, recrystallization characteristics and mechanical properties. The data obtained made it possible to analyze change in the chemical composition, sizes of intermetallic compounds and dispersoids depending on alloying elements content. The effect of the chemical composition on the driving force and the number of recrystallization nuclei was studied. It was established that the addition of alloying elements leads to grain refinement, including through the activation of a particle-stimulated nucleation mechanism. As a result, with Mg increase from 4 to 5%, addition of 0.5% Mn and 0.5% Cu, the grain size decreased from 72 to 15 µm. Grain refinement occurred due to an increase in the number of particle-stimulated nuclei, the number of which at minimal alloying rose from 3.47 × 1011 to 81.2 × 1011 with the maximum concentration of Mg, Mn, Cu additives. The retarding force of recrystallization, which in the original alloy was 1.57 × 10-3 N/m2, increased to 5.49 × 10-3 N/m2 at maximum alloying. The influence of copper was especially noticeable, the introduction of 0.5% increasing the retarding force of recrystallization by 2.39 × 10-3 N/m2. This is due to the fact that copper has the most significant effect on the size and number of intermetallic particles. It was established that strength increase without ductility change occurs when magnesium, manganese and copper content increases.

Refinement Effect and Mechanism of AZ31 Magnesium Alloy by Electromagnetic Stirring under the Effect of Grain-Refiner

Effects of Melt Treatments and Electromagnetic Stirring on the Microstructures of AZ91D Alloy

Effect of Electromagnetic Stirring and Solution Treatment on Microstructure and Properties of AZ31 Magnesium Alloy

Effects of an oscillation electromagnetic field on grain refinement and Al8Mn5 phase formation during direct-chill casting of AZ31B magnesium alloy

Grain Refinement of AZ31 Magnesium Alloy by Titanium and Low-Frequency Electromagnetic Casting

Al-CeO2-Mg refiner on grain refinement, cast fluidity and mechanical properties of AZ91 alloy

Influence of Carbon Powder and Electromagnetic Stirring on the Microstructure of AZ91D Alloy

A Novel Process for Grain Refinement of Mg-RE Alloys by Low Frequency Electro-Magnetic Stirring Assisted Near-liquidus Squeeze Casting

Grain Refinement of Magnesium Alloys Processed by Severe Plastic Deformation

Influence of Electromagnetic Stirring Processing on Microstructure and Properties of AZ91D Alloy

Grain Refinement in A Alznmgcuti Alloy by Intensive Melt Shearing: A Multi-Step Nucleation Mechanism

The Effects of Grain Refinement and Rare Earth Intermetallics on Mechanical Properties of As-Cast and Wrought Magnesium Alloys

Improvement in Grain Refinement Efficiency of Mg–Zr Master Alloy for Magnesium Alloy by Friction Stir Processing

Study on Grain Refining and Metamorphism of ZL111 Aluminium Alloys

Effects of electromagnetic stirring and subsequent homogenization treatment on the microstructure and mechanical properties of Al70Zn10Mg10Cu5Si5 multi-component alloy

Research on Grain Refinement of Sc and Zr Addition in an Al-Mg-Zn Alloy from Experiments and First-Principles Calculations

Effects and Mechanism of Ca on Refinement of AZ91D Alloy

Promotion Effect of Secondary Phase Particles on Grain Refinement of Deformed Mg–Y–Nd–Zn Alloy

Alloying Elements Effect on the Recrystallization Process in Magnesium-Rich Aluminum Alloy

Influences of Melt Treatment on Grain Sizes and Morphologies of Az91d Alloy

Effect of Abnormal Grain Refinement on Synchronous Strengthening Behavior of Fe50Mn30Co10Cr10 High Entropy Alloys