Abstract:In this study, a natural zeolite supported Co-B catalyst (Co-B/Zeolite) with a Co content of 10 wt.% was prepared by impregnation and chemical reduction method to release hydrogen gas from an alkaline sodium borohydride (NaBH 4 ) solution. The synthesized catalyst was characterized with various characterization techniques, including X-ray diffraction (XRD), X-ray fluorescence (XRF), inductively coupled plasma mass spectroscopy (ICP-MS), Brunauer–Emmett–Teller (BET), scanning electron microscopy (SEM), energy dispersive X-ray spectroscopy (EDX), Fourier transform infrared (FTIR), and X-ray photoelectron spectroscopy (XPS), etc. It was found that the BET specific surface area of Co-B/Zeolite (26.03 m 2 g −1 ) was roughly double that of the zeolite (13.12 m 2 g −1 ). The Co ratio in the catalyst was found to be 12.02 wt.% by EDX analysis. ICP-MS examination of the catalyst revealed a B/Co atomic ratio of 0.64. No peaks associated with Co-B were observed in the XRD pattern of the catalyst, indicating the amorphous nature of the component. Parameters that have significant effects on the hydrolysis reaction, such as catalyst amount, sodium hydroxide and sodium borohydride concentrations, and reaction temperature, were investigated. The hydrogen generation rate (HGR) was found to be 1732 mL min −1 g cat −1 in the presence of 100 mg of Co-B/Zeolite in 5 wt.% NaOH and 5 wt.% NaBH 4 solution at 50 °C. The experimental results were well fitted to the zero-order kinetic model ( k 0 = 0.0296–0.1619 mol min −1 g cat −1 for 20–50 °C). The activation energy ( E a ) of the catalytic reaction was found to be 44.98 kJ mol −1 . Meanwhile, the reusability evaluations showed that the catalyst preserves high stability and can still sustain 73% of its initial activity after 5 catalytic cycles.

Hydrogen Generation by Hydrolysis of Alkaline Sodium Borohydride Using a Cobalt–zinc–boron/graphene Nanocomposite Treated with Sodium Hydroxide

Hydrogen Generation and Stoichiometric Hydrolysis of Core–shell Al-Li-NaBH4 Composite

Efficient Hydrogen Generation From The Nabh4 Hydrolysis By Cobalt-Based Catalysts: Positive Roles Of Sulfur-Containing Salts

ZIF-67 Derived Cobalt-Based Catalysts for Hydrogen Generation from the Hydrolysis of Alkaline Sodium Borohydride Solution

Graphene-Modified Co-B-P Catalysts for Hydrogen Generation from Sodium Borohydride Hydrolysis

Evaluation of a Cobalt–molybdenum–boron Catalyst for Hydrogen Generation of Alkaline Sodium Borohydride Solution–aluminum Powder System

Cobalt Boride Catalysts for Hydrogen Generation from Alkaline NaBH4 Solution

Zn-MOF-74-derived graphene nanosheets supporting CoB alloys for promoting hydrolytic dehydrogenation of sodium borohydride

Hydrogen generation from catalytic hydrolysis of sodium borohydride solution using Cobalt–Copper–Boride (Co–Cu–B) catalysts

Co−O−P Composite Nanocatalysts for Hydrogen Generation from the Hydrolysis of Alkaline Sodium Borohydride Solution

Electrodeposited Co–Zn on Ni Foam As Efficient Catalysts for Hydrogen Generation from Hydrolysis of Sodium Borohydride

Catalytic Hydrogen Evolution of NaBH<sub>4</sub> Hydrolysis by Cobalt Nanoparticles Supported on Bagasse-Derived Porous Carbon

Catalytic Hydrogen Evolution of NaBH4 Hydrolysis by Cobalt Nanoparticles Supported on Bagasse-Derived Porous Carbon

Ultrafine cobalt nanoparticles supported on carbon nanospheres for hydrolysis of sodium borohydride

Effective Hydrolysis of Sodium Borohydride Driven by Self-Supported Cobalt Oxide Nanorod Array for On-Demand Hydrogen Generation

Porous Co3O4 Nanoplatelets As Efficient Catalyst Precursor for Hydrogen Generation from the Hydrolysis of Alkaline Sodium Borohydride Solution

Metal Boride-Decorated CoNi Layered Double Hydroxides Supported on Muti-Walled Carbon Nanotubes As Efficient Hydrolysis Catalysts for Sodium Borohydride

Hydrogen Generation from Alkaline NaBH4 Solution Using Co–Ni–Mo–P/γ-Al2O3 Catalysts

Efficient and Stable Co-B Catalyst Supported on Natural Zeolite for Hydrogen Generation from Hydrolysis of Alkaline NaBH4 Solution

CoO nanocrystals as a highly active catalyst for the generation of hydrogen from hydrolysis of sodium borohydride

Co-B Supported on Waxberry-Like Hierarchical Porous Carbon Microspheres: an Efficient Catalyst for Hydrogen Generation Via Sodium Borohydride Hydrolysis