Abstract:To investigate the compressive behavior of concrete under a freeze-thaw environment, porosity swelling theory, a damaged plastic model, and an element removal technique are combined to propose a novel mesoscopic numerical model of concrete. The porosity swelling theory is employed to represent the pores evolution behavior of concrete under freeze-thaw cycles, and a novel calculation method for porosity expansion is presented to characterize freeze-thaw cycle times. The damaged plastic model is used to describe the tensile and compressive features of the mortar and interface transition zone. The element removal technique with maximum damage criterion is employed to implement crack propagation. It was demonstrated that the model could capture the freeze-thaw damage and compressive failure of concrete well. The uniaxial compressive behavior of five random mesonumerical models of freeze-thaw concrete was investigated. The results showed that freeze-thaw cycles can cause tensile damage to the mortar near pores and the spalling of surface mortar. With the increase of concrete freeze-thaw cycles, the dispersion degree of the compressive stress–strain curve gradually rises, and the peak stress and peak strain of the freeze-thaw concrete stress–strain curve decrease and increase, respectively. During the freeze-thaw cycles, the sustained preload will decrease the compressive strength because it causes the microcracks to accelerate the damage induced by the freeze-thaw cycles. Then, the influence of mortar and interface transition zone properties on the compressive strength of concrete under freeze-thaw cycles was analyzed. Under 100 freeze-thaw cycles, the maximum attenuation rates of concrete compressive strength increase by 9.39% and 34.26% with the increase of interface transition zone and mortar properties, respectively. Increasing mortar properties and decreasing the sustained preload will enhance the ability of concrete to resist freeze-thaw cycles.

Interactive Effect of Mechanical Fatigue Load and the Fatigue Effect of Freeze-Thaw on Combined Damage of Concrete

Development of Internal Moisture Transfer and Cumulative Residual Strain in Concrete under Freeze-Thaw Cycles

Mesoscale Simulation of Fatigue Behavior of Concrete Materials Damaged by Freeze-Thaw Cycles

Stress Analysis for Concrete Materials under Multiple Freeze-Thaw Cycles

Study on Mechanical Properties of Deep Expansive Soil and Coupling Damage Model of Freeze–Thaw Action and Loading

Two‐dimensional Rigid Body Spring Method Based Micro‐mesoscale Study of Mechanical Strengthening/damaging Effects to Concrete by Frost Action

A Numerical Study on Chloride Diffusion in Freeze-Thaw Affected Concrete

A stochastic damage model for evaluating the internal deterioration of concrete due to freeze–thaw action

Research progress on freeze–thaw constitutive model of concrete based on damage mechanics

Experimental Study on Mechanical Properties and Pore Structure Deterioration of Concrete under Freeze–Thaw Cycles

Structural behaviors evaluation of RC beam under frost damage - A methodology with meso-macro material/bond simulation and integrating into structural analysis

Numerical Simulation of the Effect of Freeze–Thaw Cycles on the Durability of Concrete in a Salt Frost Environment

Mesoscale Simulation of Concrete Behavior with Non-Uniform Frost Damage with Verification by CT Imaging

Three-Dimensional Mesonumerical Model of Freeze-Thaw Concrete Based on the Porosity Swelling Theory

Influence of Flexural Loading on Chloride Ingress in Concrete Subjected to Cyclic Drying-Wetting Condition

Experimental investigations and micromechanical thermal fatigue models of concrete

Coupled Thermo‐hydro‐mechanical Analysis of Reinforced Concrete Beams under the Effect of Frost Damage and Sustained Load

Damage Based Constitutive Model for Predicting the Performance Degradation of Concrete

Meso-Scale Failure of Freezing–Thawing Damage of Concrete under Uniaxial Compression

Study on Freezing-Thawing damage mechanism and evolution model of concrete

The durability of concrete subject to mechanical load coupled with freeze–thaw cycles: a review