Abstract:Separating I 3 − and IO 3 − from aqueous solutions is technically challenging due to their very similar charge density. Herein, we describe the in-situ synthesis of cobalt-based layered double hydroxides (Co-LDHs) by decomposition of zeolite imidazole framework (ZIF) nanocrystals, whilst modulating the basal spacing in the Co-LDHs through anion intercalation (such as Br − , NO 3 − , and ClO 4 − ). Co-LDH-NO 3 − possesses an optimal basal spacing of ∼4.69 Å, which is slightly smaller than the van der Waals diameter of IO 3 − (∼4.79 Å), thus enabling selective adsorption of linear I 3 − (diameter ∼4.22 Å) via ion exchange in the LDH interlayer. Co-LDH-NO 3 − showed ultrafast I 3 − uptake kinetics involving strong "host-guest" interaction forces, achieving high dynamic uptake capacities of 119.94 and 127.18 mg/g in I 3 − /IO 3 − contaminated groundwater and tap water, respectively, and ∼100% separation efficiencies towards I 3 − over IO 3 − . Co-LDH-Br − with a smaller basal spacing (4.06 Å) exhibited much slower separation kinetics, and Co-LDH-ClO 4 − with a ∼5.36 Å basal spacing demonstrated poor separation efficiency under similar conditions. Ab initio molecular dynamics (AIMD) simulations were used to visually simulate the ion exchange process, with the results being consistent with the experimental observations. Furthermore, Co-LDH-NO 3 − demonstrated excellent reusability during dynamic breakthrough tests and I 3 − /IO 3 − separation cycles due to a "special memory effect" of the 2D interlayer. This work guides adsorbent design for the efficient removal and separation of iodine species from contaminated water.

Materials Design and Control Synthesis of the Layered Double Hydroxide with the Desired Basal Spacing

Prediction and Synthesis of Novel Layered Double Hydroxide with Desired Basal Spacing Based on Relevance Vector Machine

Data mining assisted materials design of layered double hydroxide with desired specific surface area

Long-Range and Short-Range Structures of Multimetallic Layered Double Hydroxides

A Green Route for the Preparation of Layered Double Hydroxides from Basic Magnesium Carbonate

Efficient, scalable, closed-loop synthesis of highly crystalline pure phase MgAl-layered double hydroxides intercalated with hydroxyl anions

Ionothermal Synthesis Of Cobalt Iron Layered Double Hydroxides (Ldhs) With Expanded Interlayer Spacing As Advanced Electrochemical Materials

Synthesis of Well-Dispersed Layered Double Hydroxide Core@Ordered Mesoporous Silica Shell Nanostructure (ldh@msio(2)) and Its Application in Drug Delivery

Dispersion and Size Control of Layered Double Hydroxide Nanoparticles in Aqueous Solutions

One-Step Synthesis of Layered Double Hydroxides by a Solvent-Free Method

Morphological Control of Layered Double Hydroxides Prepared by Co-Precipitation Method

New Synthetic Route to Mg–Al–CO3 Layered Double Hydroxide Using Magnesite

A General and Scalable Formulation of Pure Caal-Layered Double Hydroxide Via an Organic/Water Solution Route

Remote Synthesis of Layered Double Hydroxide Nanosheets Through the Automatic Chemical Robot

Selective Covalent Basal Plane Modification as a Probe of Hydroxide Ion Conduction Pathways in Magnesium Aluminum Layered Double Hydroxides

In-situ synthesis of layered double hydroxides with tunable basal spacing for efficient iodide over iodate adsorption selectivity

A Facile Method to Prepare Layered Manganese Oxides with Large Interplanar Spacing

Variations in chloride ion sorption within Layered double hydroxides engineered with different cation types

Synthesis of Elevated Temperature CO2 Adsorbents from Aqueous Miscible Organic-Layered Double Hydroxides

Contribution of Sodium Dodecyl Sulphate and Sodium Lauric Acid in the One-Pot Synthesis of Intercalated ZnAl-layered Double Hydroxides

Analysis of the oxygen evolution activity of layered double hydroxides (LDHs) using machine learning guidance