Abstract:Inconel 718 has good fabricability, high strength at elevated temperatures, and high corrosion resistance and is widely deployed in many aerospace and other high-performance applications. With the molten pool's rapid solidification during laser powder bed fusion (LPBF), the resulting microstructures differ from those expected in equilibrium conditions. Residual stresses, microsegregation, anisotropy, undesirable phases, layered structure, and lower mechanical properties are the challenges that must be addressed before LPBF-ed Inconel 718 parts can be industrially implemented. Heat treatment of Inconel 718 after the LPBF process is widely discussed in the literature, and the proposed heat treatment processes do not address all the challenges mentioned above. For this reason, specific heat treatments should be designed to achieve desired mechanical properties. Four different high-temperature heat treatment procedures were developed and tested in recent work to study the effect of various heat treatment parameters on the type of precipitates, grain size, room and elevated temperature mechanical properties, and creep properties of LPBF-ed Inconel 718. Two heat treatment procedures were designed to study the effect of eliminating the stress relief cycle and increasing the soaking time of solution heat treatment at the same hot isostatic pressing (HIP) and aging conditions. The other two heat treatment procedures were designed to study the effect of stress relief and aging parameters, with similar HIP and solution annealing parameters. The investigated heat treatment procedures showed the formation of equiaxed grain size and a significant amount of γ ′′ particles at the grain boundary in addition to primary carbide types (MC). Three different grain sizes could be obtained, starting with the same as-built microstructure by controlling post-process heat treatment parameters. The first type, coarse grain size (ASTM grain size No. G 3), suitable for creep application, was achieved by increasing the soaking time at the aging cycle. The second type, the formation of serrated grain boundaries suitable for good fatigue and creep properties, was achieved by decreasing the stress relief cycle's soaking time and temperature. The third type, fine grain size (ASTM grain size No. G 6), which is preferable for fatigue properties, was achieved by decreasing the soaking time at the solution annealing cycle. Among the different heat treatment conditions, the heat treatment with lower stress relief temperature and longer soaking time at solution annealing steps showed compromised equiaxed grain size with serrated grain boundaries, and it was selected for mechanical testing. The mechanical properties at room and elevated temperature (650 °C) and creep properties under constant axial stress of 690 MPa at 650 °C until failure were evaluated. The obtained elongation is > 2 × higher than the available properties in the AMS 5663 for wrought Inconel 718, AMS 5383 for cast Inconel 718, and ASTM F3055 for LPBF while maintaining a higher tensile strength above the average level found in the standards. It can be concluded that the performed heat treatment achieves higher mechanical properties. The values of UTS, YS, elongation, and reduction of area percentages are similar in the Z and XY orientations, revealing the presence of isotropic microstructure and uniform distribution of MC and γ ′′ precipitates.

Heat Treatment of a Candidate Material for 700 °C A-USC Power Plants

Optimization of the Post-Heat Treatment of Additively Manufactured IN718

Improving High-Temperature Mechanical Properties of Additively Manufactured Inconel 718 Through Heat Treatment

Microcrack Nucleation and Propagation Investigation of Inconel 740H Alloy under in Situ High Temperature Tensile Test

Microstructure Evolution and Mechanical Properties of Inconel 740H During Aging at 750 °C

Effect of heat treatment on the anisotropic mechanical properties and corrosion resistance of laser powder bed fusion fabricated Inconel 625

Influence of stabilization heat treatment temperature on microstructure and stress rupture properties of Inconel 706 superalloy

Thermodynamic Evaluation and Composition Design of Candidate Alloys for 700 ℃ Class Ultra-supercritical Plant

Knowledge of process-structure-property relationships to engineer better heat treatments for laser powder bed fusion additive manufactured Inconel 718

The effect of homogenization temperature on the microstructure and high temperature mechanical performance of SLM-fabricated IN718 alloy

Influence of Heat Treatment on Cyclic Response of Nickel-Based Superalloy Inconel 718 up to Very-High Cycle Regime

Effect of heat treatment on microstructure and mechanical properties of selective laser melted Inconel 718 alloy

Effect of Solution and Aging Heat Treatment on the Microstructure and Mechanical Properties of Inconel 625 Deposited Metal

The Application of Grain Boundary Engineering to a Nickel Base Superalloy for 973 K (700 °C) USC Power Plants

Isothermal Solid‐State Transformations of Inconel 718 Alloy Fabricated by Selective Laser Melting

Heat treatment for selective laser melting of Inconel 718 alloy with simultaneously enhanced tensile strength and fatigue properties

Achieving High Strength and Creep Resistance in Inconel 740H Superalloy through Wire-Arc Additive Manufacturing and Thermodynamic-Guided Heat Treatment

Effects of a modified heat-treatment on microstructure and mechanical properties of additively manufactured Inconel 718

Effect of Heat Treatment Temperature on Microstructure, Tensile Properties and δ-Precipitate Phase in Ni-based Superalloy

Effects of post heat treatment on the microstructure evolution of Inconel 718 manufactured by selective laser melting

Influence of heat treatment on Inconel 625 superalloy sheet: carbides, γ'', δ phase precipitation and tensile deformation behavior