Abstract:In this study, various diamine monomers were used to synthesize aramid polymer films via a low-temperature solution condensation reaction with diacid chloride. For diamines with relatively high basicity, the reaction system became opaque because amine salt formation inhibited polymer synthesis. Meanwhile, low-basicity diamines with strong electron-withdrawing groups, such as CF3 and sulfone, were smoothly polymerized without amine salt formation to provide highly viscous solutions. The acid byproduct HCl generated during polymerization was removed by adding propylene oxide to the reaction vessel and converting the acid into highly volatile inert substances. The resulting solutions were used as varnishes without any additional purification, and polymer films with an excellent appearance were easily obtained through a conventional casting and convection drying process. The films neither tore nor broke when pulled or bent by hand; furthermore, even when heated up to 400 °C, they did not decompose or melt. Moreover, polymers prepared from 2,2-bis(trifluoromethyl)benzidine (TFMB) and bis(4-aminophenyl)sulfone (pAPS) did not exhibit glass transition until decomposition. The prepared polymer films showed a high elastic modulus of more than 4.1 GPa and a high tensile strength of more than 52 MPa. In particular, TFMB-, pAPS-, and 2,2-bis(4-aminophenyl)hexafluoropropane-based polymer films were colorless and transparent, with very high light transmittances of 95%, 96%, and 91%, respectively, at 420 nm and low yellow indexes of 2.4, 1.9, and 4.3, respectively.

Preparation of Smooth Polymer Thin Film Using Spray Method under Vacuum

Vacuum Spray Method for Semiconductor Polymer Thin Film Preparation

Synthesis of Polymer Thin Film Gradient with Nanometer Thickness through Water Diffusion Controlled Surface Polymerization

Preparation of polymer thin films with controlled in depth dye distributions

Solventless Polymerization at the Gas–Solid Interface to Form Polymeric Thin Films

Fabrication of Polymer Thin Films with In-Depth Dye-Dispersed Structures by the Vacuum Spray Method

Preparation of Poly(Methylmethacrylate)/Layered Double Hydroxides Nanocomposites Via in Situ Solution Polymerization

Polymer Solar Cell Prepared by A Novel Vacuum Spray Method

Preparation of Poly (methyl Methacrylate)/nanometer Calcium Carbonate Composite by In-Situ Emulsion Polymerization

Preparation of Porous Pmma Resin by A New Emulsion Polymerization Process and the Mechanism of Particle Formation

Preparation and morphology control of amphiphilic block copolymer thin films using mixed solvent vapors

Facile Preparation of Light Refractive Poly(Aroxycarbonyltriazole)S by Metal-Free Click Polymerization

Preparation of uniform microcapsules with silicone oil as continuous phase in a micro-dispersion process.

Interface Structures Between Polymer Substrates and Fluorescent Dye-Doped Polymer Layers Formed by Vaporization in Vacuum

Preparation of Polyethylene and Ethylene/Methacrylic Acid Copolymer Blend Films with Tunable Surface Properties through Manipulating Processing Parameters during Film Blowing

In Situ Copolymerized Toughened Polymethyl Methacrylate (PMMA) with Highly Transparency for Support Film of Polarizers

FORMATION OF VORONOI PATTERN IN PMMA/PS BLEND THIN FILMS

Preparation and Properties of Mechanically Robust, Colorless, and Transparent Aramid Films

MORPHOLOGY OF SOLUTION CAST PS/PMMA BLEND FILMS

Preparation of vertically oriented aromatic polyester thin films by thermal chemical vapor deposition

Morphology Development Of Ultrathin Symmetric Diblock Copolymer Film Via Solvent Vapor Treatment