Abstract:A series of dealuminated zeolites Y with framework n(Si)/n(Al) ratios of 2.8-6.0 was prepared by steaming and characterized by atomic emission spectroscopy and H-1, Al-27, and Si-29 NMR spectroscopy. The steaming of zeolite H-Y was performed under water vapor pressures of 3.4-81.5 kPa and at a temperature of 748 K. To exclude an additional modification of the dealuminated zeolites Y, the samples were investigated in the nonhydrated state, i.e., without hydration after the dealumination. By Si-29 magic-angle spinning (MAS) NMR spectroscopy, a strong high-field shift of the signals of Si(3Al) and Si(2Al) sites in the spectra of nonhydrated zeolites Y in comparison with those of the hydrated samples was observed. This finding is explained by a change of the Si-O-T bond angles of Si(nAl) sites in the local structure of nonhydrated framework AlO4 tetrahedra. With increasing water vapor pressure during the dealumination, a systematic decrease of the total amounts of framework aluminum atoms in nonhydrated zeolites Y was found by Al-27 spin-echo NMR and 29Si MAS NMR spectroscopies. The amounts of disturbed framework aluminum atoms, probably 3-fold-coordinated species in nonhydrated zeolites Y. were determined by the increase of the concentrations of bridging OH groups after an ammonia adsorption/desorption treatment and by application of 1H MAS NMR spectroscopy. By a quantitative comparison of the amounts of tetrahedrally coordinated framework aluminum atoms, responsible for the occurrence of negative framework charges, and the amounts of charge-compensating residual sodium cations and bridging hydroxyl protons, the mean cationic charge of extraframework aluminum atoms was estimated. This mean cationic charge per extraframework aluminum atom was found to vary from ca. +2 for weakly dealuminated zeolites Y to ca. +0.5 for strongly dealuminated samples.

Investigation of Aluminum Site Changes of Dehydrated Zeolite H-Beta During a Rehydration Process by High-Field Solid-State NMR

Characterization of Framework and Extra-Framework Aluminum Species in Non-Hydrated Zeolites Y by 27al Spin-Echo, High-Speed MAS, and MQMAS NMR Spectroscopy at B0 = 9.4 to 17.6 T.

State of Aluminum in Dealuminated, Nonhydrated Zeolites Y Investigated by Multinuclear Solid-State Nmr Spectroscopy

Investigation of the Microporous Structure and Non-Framework Aluminum Distribution in Dealuminated Nanosized HZSM-5 Zeolite by 129xe NMR Spectroscopy

27Al MAS NMR Studies of HBEA Zeolite at Low to High Magnetic Fields

MAS NMR Studies on the Dealumination of Zeolite MCM-22

An Investigation of the Roles of Surface Aluminum and Acid Sites in the Zeolite Mcm-22

Effects of Adsorbate Molecules on the Quadrupolar Interaction of Framework Aluminum Atoms in Dehydrated Zeolite H,Na-Y.

Enhanced Resolution of Aluminum and Proton Sites in the Molecular Sieve SAPO-37 by 27al Multiple Quantum Magic Angle Spinning and 1H Spin Echo Editing NMR

Solid-state NMR Study on Dealumination Mechanism of H-MOR Zeolite by High-Temperature Hydrothermal Treatment

A high‐resolution solid‐state NMR study on nano‐structured HZSM‐5 zeolite

Local Structure of Framework Aluminum in Zeolite H−ZSM-5 During Conversion of Methanol Investigated by in Situ NMR Spectroscopy

29Si and 27Al MAS NMR characterization of non-hydrated zeolites Y upon adsorption of ammonia

27Al Multiple Quantum MAS NMR Study on the Distribution of Aluminium in the Zeolite MCM-22

Effect of Dehydration on the Local Structure of Framework Silicon Atoms in Zeolites Y Investigated by Solid‐State NMR Spectroscopy

Toward the Aluminum Coordination in Dealuminated Mordenite and Amorphous Silica–alumina: A High Resolution 27al MAS and MQ MAS NMR Study

Effect of Surface Methoxy Groups on the 27al Quadrupole Parameters of Framework Aluminum Atoms in Calcined Zeolite H–Y

Revealing the Bronsted Acidic Nature of Penta-Coordinated Aluminum Species in Dealuminated Zeolite Y with Solid-State NMR Spectroscopy

CHEMICAL STATE OF NON-FRAMEWORK ALUMINUM IN USY ZEOLITE AND ITS INFLUENCE ON ZEOLITE ACIDITY

Detection of Distorted Tetrahedral-Coordinate Aluminum in Dealuminated Mordenite by ~(27)al 3Q MAS NMR

Flexible Al Coordination with H2O Explaining the Deviation of Strong Acid Amount from the Framework Al Content in Al-Rich SSZ-13