Improved Catalytic Performance in Dimethyl Ether Carbonylation over Hierarchical Mordenite by Enhancing Mass Transfer
Shuaipeng Liu,Zaizhe Cheng,Ying Li,Junhao Sun,Kai Cai,Shouying Huang,Jing Lv,Shengping Wang,Xinbin Ma
DOI: https://doi.org/10.1021/acs.iecr.0c01156
2020-06-15
Abstract:Dimethyl ether (DME) carbonylation over mordenite (MOR) is a typical spatial confined reaction, but the superior shape selectivity is accompanied by a diffusion limitation of the microporous channel. Thus, enhancing mass transfer to improve the catalytic performance of MOR is important for its application. In this study, an unbiased chemical etching with a NH<sub>4</sub>F solution was employed to introduce secondary porosity into MOR. Through altering the etching temperature, a series of hierarchical MOR with different porosities were successfully prepared. XRD, Ar adsorption, and ICP together with the quantification of acid sites confirmed that the microporous structure and acidity of pristine zeolite were preserved after etching. The Weisz–Prater criterion was used to assess the internal diffusion limitation of DME and methyl acetate (MA). Moreover, toluene was chosen as a representative molecule in zero length column measurements, in order to explore the mass transfer of coke precursors in pristine and modified MOR. Combining the catalytic performance (i.e., TOF<sub>MA</sub>, selectivity, and deactivation rate constant) and diffusivity of molecules within MOR, we obtain insight into the influence of diffusion on zeolite-catalyzed DME carbonylation.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acs.iecr.0c01156?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acs.iecr.0c01156</a>.ZLC setup, data analysis, fitting curves, derived parameters, selectivity of byproducts over MOR-P and MOR-<i>T</i>, characterizations of spent catalysts, and comparison of catalytic activity of H-MOR in literature and this work (<a class="ext-link" href="/doi/suppl/10.1021/acs.iecr.0c01156/suppl_file/ie0c01156_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
engineering, chemical