White-light Emitting and Energy Transfer Mechanism in the Ce3+, Tb3+ and Eu3+ Co-Doped Sr2MgSi2O7 Phosphor
Wu Jing,Zhang Ji-Lin,Zhou Wen-Li,Rong Chun-Ying,Yu Li-Ping,Li Cheng-Zhi,Lian Shi-Xun
DOI: https://doi.org/10.7503/cjcu20120211
2013-01-01
Abstract:Sr2MgSi2O7 : Ce3+, Tb3+, Eu3+ phosphors were prepared by high temperature solid state reaction. Crystallization and optical properties were investigated via powder X-ray diffraction and fluorescence spectra, respectively. Under the excitation of ultraviolet(327 nm), the emission spectra of these phosphors exhibited multi-emission lines peaked at about 387 (blue-purple color), 542(green color) and 611 nm (red color). Monitored at 387, 542 and 611 nm, respectively, the Sr2MgSi2O7 : Ce3+, Tb3+, Eu3+ powder got optimally excited at lambda(ex) = 327 nm, the Sr2MgSi2O7 Tb3+ powder got optimally excited at lambda(ex) = 235 nm. It has been found that the chromaticity coordinates (0. 337, 0. 313) for the nominal composition Sr-1.91 MgSi2O7 : 0.01Ce(3+), 0.05Tb(3+),0.03Eu(3+) is very close to the CIE (Commission International de I' Eclairage 1931 chromaticity) standard white coordinates (0.33, 0.33), showing that Sr1.91MgSi2O7 : 0.01Ce(3+), 0.05Tb(3+), 0.03Eu(3+) is a potential single-phased white phosphor for LED-based UV-chip. The energy transfer processes from Ce3+ to Tb3+ and from Ce3+ to Eu3+ were discussed. There may be two kinds of energy transfer process in the Sr2MgSi2O7 : Ce3+,Tb3+,Eu3+ system, which is from Ce3+(5d) to Eu3+ (D-5(4)) +Tb3+(D-5(4)) and Tb3+(D-5(2,3))-> Ce3+(5d)-> Eu3+(L-5(6)).