Abstract:Reported herein is a chiral resolution polysulfone membrane prepared via mussel-inspired chemistry. Polysulfone membranes were modified with dopamine, which underwent in situ polymerization on the membrane substrate, and β-cyclodextrin was used as a chiral selector. The preparation conditions were optimized and the resultant membrane obtained under these conditions showed desirable water permeability (~24.0L/(m2·h·bar)) and surface hydrophilicity (contact angle is lower than 37.1±3.4°). The polydopamine layer exhibited desirable stability in a series of aqueous solutions with pH values ranging from 4.0–6.0 or in isopropanol for less than an hour (detachment ratio was lower than 1.2%). Characterization of the surface morphology and XPS elemental analysis revealed that the membrane surface was fully coated by polydopamine and a β-cyclodextrin monolayer formed on the surface of the polydopamine coating. The grafting density of β-cyclodextrin calculated from the XPS results was ~11.5mg/m2. The optimal pH value for the resolution of D- or L-tryptophan feed solution was 5.90 and a low concentration of the feed solution provided a high resolution efficiency. The enantiomeric excess (e.e.) value of the membrane for Trp racemic mixture achieved to ~3.2% with the feed solution of tryptophan racemic mixture was 5×10−5mol/L and the operating pressure was 0.1MPa. After 3 times of isopropanol-washed regeneration processes, the e.e. value was still stable around to ~3%. The mussel-inspired chemically modified membrane exhibited the same mechanical properties as the purely polysulfone-based membrane. The methods and results provided in this paper may facilitate the large-scale production of chiral resolution membranes or other chiral separation membranes with higher performance.

Optical Resolution Membranes from Polysulfones Bearing Alanine Derivatives as Chiral Selectors

Electrospun nanofiber membranes from polysulfones with chiral selector aimed for optical resolution

Chiral separation membranes from modified polysulfone having myrtenal-derived terpenoid side groups

Chiral Resolution by Polysulfone-Based Membranes Prepared Via Mussel-Inspired Chemistry

Carboxylated Polysulfone Membranes Having a Chiral Recognition Site Induced by an Alternative Molecular Imprinting Technique

A novel approach to chiral separation: thermo-sensitive hydrogel membranes

Chiral separation with molecularly imprinted polysulfone-aldehyde derivatized nanofiber membranes☆

Preparation and application of novel polysulfone chiral membranes for the separation of tryptophan enantiomers

Molecularly Imprinted Chitosan Membrane for Chiral Resolution of Phenylalanine Isomers

Preparation and Evaluation of Chiral Selective Cation-Exchange Membranes

Preparation of chiral selective membranes for electrodialysis separation of racemic mixture

Molecularly Imprinted Organic–inorganic Hybrid Membranes for Selective Separation of Phenylalanine Isomers and Its Analogue

Helical screw sense bias in chiral polyfluorene stimulated by solvent

Preparation of CS/GPTMS hybrid molecularly imprinted membrane for efficient chiral resolution of phenylalanine isomers

Enantioselective transport of optical isomers via chiral polysaccharide membrane

Mesomorphic Behavior and Optical Properties of Liquid‐crystalline Polysiloxanes Bearing Different Chiral Groups

Synthesis and Properties of Side-Chain Liquid Crystalline Polymers Grafted with Chiral Dimers Containing Cholesteryl Groups

Preparation of Chiral Selective Anion-Exchange Membranes and Their Resolution Performances

Optically active copolymers of N-(oxazolinyl)phenylmaleimides with methyl methacrylate: Synthesis and chiral recognition ability

Chiral Polymers of Intrinsic Microporosity: Selective Membrane Permeation of Enantiomers

SYNTHESIS AND CHIRAL RECOGNITION ABILITY OF OPTICALLY ACTIVE POLY(METHACRYLAMIDE) WITH SIDE CHAINS