Abstract:Reported herein is a chiral resolution polysulfone membrane prepared via mussel-inspired chemistry. Polysulfone membranes were modified with dopamine, which underwent in situ polymerization on the membrane substrate, and β-cyclodextrin was used as a chiral selector. The preparation conditions were optimized and the resultant membrane obtained under these conditions showed desirable water permeability (~24.0L/(m2·h·bar)) and surface hydrophilicity (contact angle is lower than 37.1±3.4°). The polydopamine layer exhibited desirable stability in a series of aqueous solutions with pH values ranging from 4.0–6.0 or in isopropanol for less than an hour (detachment ratio was lower than 1.2%). Characterization of the surface morphology and XPS elemental analysis revealed that the membrane surface was fully coated by polydopamine and a β-cyclodextrin monolayer formed on the surface of the polydopamine coating. The grafting density of β-cyclodextrin calculated from the XPS results was ~11.5mg/m2. The optimal pH value for the resolution of D- or L-tryptophan feed solution was 5.90 and a low concentration of the feed solution provided a high resolution efficiency. The enantiomeric excess (e.e.) value of the membrane for Trp racemic mixture achieved to ~3.2% with the feed solution of tryptophan racemic mixture was 5×10−5mol/L and the operating pressure was 0.1MPa. After 3 times of isopropanol-washed regeneration processes, the e.e. value was still stable around to ~3%. The mussel-inspired chemically modified membrane exhibited the same mechanical properties as the purely polysulfone-based membrane. The methods and results provided in this paper may facilitate the large-scale production of chiral resolution membranes or other chiral separation membranes with higher performance.

Electrospun nanofiber membranes from polysulfones with chiral selector aimed for optical resolution

Optical Resolution Membranes from Polysulfones Bearing Alanine Derivatives as Chiral Selectors

Chiral separation with molecularly imprinted polysulfone-aldehyde derivatized nanofiber membranes☆

Chiral separation membranes from modified polysulfone having myrtenal-derived terpenoid side groups

Tailoring the Selectivity of Quasi-Pims Nanofiltration Membrane Via Molecular Flexibility of Acyl Chloride Monomers for Desalination from Dye Effluents

Electrospinning of Cellulose Benzyl Carbamates for Enantioselective Membrane Filtration

Chiral Resolution by Polysulfone-Based Membranes Prepared Via Mussel-Inspired Chemistry

Molecularly Imprinted Nanofiber Membranes from Carboxylated Polysulfone by Electrospray Deposition

Precise Sieving of Chiral Molecules by a Crosslinked Cyclodextrin-Cellulose Nanofiber Composite Membrane

High Flux and Rejection with Chiral Chitosan Composite Nanofiltration Membranes: Preparation and Characterization

Carboxylated Polysulfone Membranes Having a Chiral Recognition Site Induced by an Alternative Molecular Imprinting Technique

Preparation and application of novel polysulfone chiral membranes for the separation of tryptophan enantiomers

Chiral Polymers of Intrinsic Microporosity: Selective Membrane Permeation of Enantiomers

Chiral mixed matrix membrane with (S,S)- Whelk-O®1 selector supported on polyethersulfone/MCM-41

Preparation of chiral selective membranes for electrodialysis separation of racemic mixture

Preparation and Evaluation of Chiral Selective Cation-Exchange Membranes

Cyclodextrin Metal-Organic Framework-Polymer Composite Membranes Towards Ultimate and Stable Enantioselectivity

New Chiral Catalytic Membranes Created by Coupling UV-Photografting with Covalent Immobilization of Salen–Co(III) for Hydrolytic Kinetic Resolution of Racemic Epichlorohydrin

Fabrication of PVDF-blended ultrafiltration membranes incorporated by chiral mesoporous silica for enantioseparation

A Homochiral Porous Organic Cage‐Polymer Membrane for Enantioselective Resolution

Homochiral MOF–Polymer Mixed Matrix Membranes for Efficient Separation of Chiral Molecules