Abstract:Owing to the superparamagnetic iron oxide nanoparticles' wide applications, a new approach in the synthesis of mainly superparamagnetic iron oxide nanoparticles is reported. The Fe3O4 nanoparticles (similar to 500 nm) were synthesised through the carbon reduction method, which is a brand new method. The best parameters of synthesis of the nanoparticles are fixed through characterising by transmission electron microscope (TEM), X-ray diffraction and a vibrating sample magnetometer of the Fe3O4 nanoparticles obtained under different experimental conditions. The TEM characterisation results show that the best ratio of the carbon and ferric chloride is 3:1 and the most suitable heating time is 3 h. The nanoparticles, which were obtained with furnace cooling under vacuum condition after 3 h heating, have the best magnetic properties and most stable crystal from. The characterisations of SiO2 protected nanoparticles demonstrate that the component of the nanoparticles is Fe3O4. The UV-vis absorption spectrum of the Fe3O4 nanoparticles demonstrates wide-range light absorption of the Fe3O4 nanoparticles. Moreover, quantitative analysis of this new method is conducted to confirm repeatability. The actual qualities of the Fe3O4 nanoparticles are always consistent with the theoretical ones, which indicate that the repeatability of this method is excellent.

Facile Synthesis of Fe3O4 Nanoparticles with a High Specific Surface Area

Synthesis of Fe3O4 Nanoparticles and Their Magnetic Properties

Synthesis of Fe3O4 Nanoparticles by Co-precipitation and Micro-reactor Method

Facile Synthesis of Fe3O4/SiO2 Composite Nanoparticles from Primary Silica Particles

Chemical Synthesis of Magnetic Fe<sub>3</sub>O<sub>4</sub> Nanoparticles

Reclamation of acid pickling waste: A facile route for preparation of single-phase Fe 3 O 4 nanoparticle

Facile Synthesis Of Superparamagnetic Fe3o4 Nanoparticles Just Using Ferric Citrate And Water

Preparation and Surface Modification of Monodisperse Fe3O4 Nanoparticles

A Facile Synthetic Pathway of Monodisperse Fe3O4 Nanocrystals

Generalized and Facile Synthesis of Fe3O4/MS (M = Zn, Cd, Hg, Pb, Co, and Ni) Nanocomposites

Synthesis of Superparamagnetic Iron Oxide Nanoparticles in Carbon Reduction Method

Fabrication of Fe 3 O 4 @APF Magnetic Nanospheres with Tunable Core–Shell Structure: an Effective Carrier and Reducing Agent for Ag Nanoparticles

Preparation and Surface Modification of Magnetic Fe3O4 Nanoparticles

Facile Synthesis of Superparamagnetic Fluorescent Fe3O4/ZnS Hollow Nanospheres

Fabrication of Fe3O4@APF Magnetic Nanospheres with Tunable Core–Shell Structure: An Effective Carrier and Reducing Agent for Ag Nanoparticles

Ultrasonic-assisted synthesis of amorphous Fe 3 O 4 with a high specific surface area and improved capacitance for supercapacitor

Synthesis of Fe3O4 Nanoparticles and Preparation of Magnetic Fluids

Preparation of Fe3O4 with High Specific Surface Area and Improved Capacitance As a Supercapacitor

Synthesis and Characterization of Monodisperse Fe3O4Nanospheres with Uniform Particle Size Distribution by a Simple Solvothermal Method

Synthesis of Fe$_3$O$_4$ nanoparticles and their magnetic properties

Highly Ordered Self-Assembly with Large Area of Fe3O4 Nanoparticles and the Magnetic Properties.