Abstract:A combined steady-state and transient approach is employed to investigate the corrosion behavior of X80 pipeline steel in carbon dioxide-saturated brines. Continuous bubbling of carbon dioxide into a test vessel with 1 liter capacity is performed to simulate the flowing condition. The measurement of time-dependent open-circuit potential, polarization resistance, and electrochemical impedance spectroscopy (EIS) is conducted to interpret the evolution of dissolution processes at the corroding interface. Three distinguishing stages are observed at a temperature of 60 °C during a whole exposure of 144 h. Analyses mainly based on the consecutive mechanism show that after the first stage of the active-adsorption state, the anodic reaction is significantly retarded by the accumulation of (FeOH)ads on the iron surface, causing a sharp increase in the polarization resistance and the open-circuit potential, as well as the disappearance of the inductive loop in EIS. At the third stage, the formation of the corrosion product layer similarly reduces both the anodic and cathodic reactions, which arouses a linear increase in the polarization resistance with time and a capacitive loop in EIS but changes the open-circuit potential slightly. An increase in salinity in this study reduces the polarization resistance and enhances iron dissolution by promoting the formation and relaxation of (FeOH)ads; however, it brings little change to the developing time of the three stages obviously. At a low temperature of 20 °C, a protective product layer is not observed in carbon dioxide-saturated brine, and the dissolution of iron is mainly under activation control during the whole exposure. A notable enlarged polarization resistance and different interfacial processes are observed in an alkaline solution compared with those in acidic environments, which is deduced to be resulted from an impedance in the relaxation of (FeOH)ads by increasing pH. The observations in this study support well that the iron dissolution reaction at the initial stage exposed in carbon dioxide aqueous environments is dominant by water adsorption on the iron surface, and further investigation should be performed on the role that carbon dioxide plays in the evolution of corrosion products and the formation of a protective film on the steel surface by taking into account local water chemistry.

Effect of pH Value on the Crack Growth Behavior of X70 Pipeline Steel in the Dilute Bicarbonate Solutions

Microstructural Effects in the Development of Near-Neutral pH Stress Corrosion Cracks in Pipelines

Determinants of health-promoting lifestyles in older persons.

ELECTROCHEMICAL CHARACTERISTICS OF X70 PIPELINE STEEL IN A SYNTHETIC NEAR NEUTRAL SOIL SOLUTION

Influences of Temperature and pH Value on the Corrosion Behaviors of X80 Pipeline Steel in Carbonate/Bicarbonate Buffer Solution

Anodic Dissolution Characteristics of the X80 Pipeline Steel in Simulated Soil Solution

Investigation of the Effect of pH on Stress Corrosion Cracking of API 5L X65 Steel by Impedance Spectroscopy and Slow Strain Rate Tensile Test

pH Effect of Natural Gas Hydrate on X80 Steel Solid—Liquid Phase Scouring Corrosion

Effects of Temperature and Applied Potential on the Stress Corrosion Cracking of X80 Steel in a Xinzhou Simulated Soil Solution

Understanding the interaction between erosion and corrosion of pipeline steel in acid solution of different pH

Blunt and penetrating trauma--has anything changed?

Accelerating Effect and Critical Ph Value of Occluded Cell Corrosion Within Pits, Crevices, or Stress Corrosion Cracks

Stress corrosion cracking behavior induced by Sulfate-reducing bacteria and cathodic protection on X80 pipeline steel

Corrosion characteristics of simulated reheated heat-affected-zone of X80 pipeline steel in carbonate/bicarbonate solution

Effects of cathodic protection potential on microbiologically induced corrosion behavior of X70 steel in a near-neutral pH solution

CRACK PROPAGATION QUANTITATIVE MODELS OF X70 PIPELINE STEEL IN THE SYNTHETIC SOIL SOLUTION

Initiation of Stress Corrosion Cracks in X80 and X100 Pipe Steels in Near-Neutral Ph Environment

Experimental Investigation on Corrosion Behavior of X80 Pipeline Steel under Carbon Dioxide Aqueous Conditions

Corrosion Behavior of X70 Pipeline Steel in 3.5% Nacl Solution under the Synergistic Action of Cathodic Protection and Sulfate- reducing Bacteria

Properties of Surface Film on X70 Pipeline Steel in CO3^2-／HCO3^- Environment

Effect Of Temperature On Corrosion Behaviour Of X70 Steel In High Pressure Co2/So2/O-2/H2o Environments