Abstract:In recent years, TiO2(B) has been widely used in photocatalysis, electrocatalysis, and lithium-ion batteries due to its unique crystal structure. However, as a metastable phase semiconductor, TiO2(B) is prone to transform into the stable anatase or rutile phase at high temperature. Therefore, the low crystallinity of TiO2(B) was usually formed at low temperature. Both of the above two concerns restrict its application in photocatalysis. In this research, we found that an appropriate amount of HF could inhibit the phase transformation process from TiO2(B) to anatase. XRD patterns and Raman spectra showed that when 0.3 wt % HF was added prior to the calcination, a large amount of TiO2(B) could be maintained even at 750 degrees C. Thus, the sample with TiO2(B)/anatase heterophase junction structure was obtained at high temperature, which exhibited the enhanced photocatalytic activity both for pollution degradation and hydrogen production. The phase transformation mechanism was finally revealed by DFT calculations. It was demonstrated that the F anions adsorbed on the surface of TiO2(B) could efficiently decrease the surface energy from 0.63 J/m(2) for the clean surface to -0.22 J/m(2) for the F anions adsorbed surface, which was the internal factor for the retarded phase transformation process and promoted the fabrication of heterophase junction at high temperature.

Engineering highly active TiO 2 photocatalysts via the surface-phase junction strategy employing a titanate nanotube precursor

Surface roughening and top opening of single crystalline TiO2 nanowires for enhanced photocatalytic activity

Surface Defect-Controlled Growth and High Photocatalytic H-2 Production Efficiency of Anatase TiO2 Nanosheets

(001)-Exposed TiO2 Microcrystals Decorated with Few-Layer Nanobelts for Enhanced Photocatalytic Activity

Engineering of anatase/rutile TiO2 heterophase junction via in-situ phase transformation for enhanced photocatalytic hydrogen evolution

Acid-regulated hydrolysis and condensation of titanium cation toward controllable synthesis of multiphase mesoporous TiO2 for effectively enhance photocatalytic H2 evolution

Controlling Surface and Interface of Tio2 Toward Highly Efficient Photocatalysis

Highly Efficient Photocatalysts for Surface Hybridization of TiO2 Nanofibers with Carbon Films

Preparation of Porous TiO2 Photocatalyts with Different Crystal Phases and High Catalytic Activity by Simple Calcination of Titanate Nanofibers

Hierarchical Nanotubular Anatase/Rutile/TiO2(B) Heterophase Junction with Oxygen Vacancies for Enhanced Photocatalytic H2 Production.

Titanium Dioxide Nano-Heterostructure with Nanoparticles Decorating Nanowires for High-Performance Photocatalysis

In-situ formation of SrTiO3/Ti3C2 MXene Schottky heterojunction for efficient photocatalytic hydrogen evolution

rous TiO 2 photocatalyts with di ff erent crystal phases and high catalytic activity by simple calcination of titanate nano fi bers †

Regulating Phase Junction and Oxygen Vacancies of TiO2 Nanoarrays for Boosted Photoelectrochemical Water Oxidation

Direct Z-scheme g-C3N4/TiO2 heterojunction porous nanotubes: An ingenious synthesis strategy to enhance photocatalytic activity

Rutile-Coated B-Phase TiO2 Heterojunction Nanobelts for Photocatalytic H2 Evolution

Enhanced photocatalytic activity of hierarchical titanium dioxide microspheres with combining carbon nanotubes as "e-bridge"

Regulating Phase Junction and Oxygen Vacancies of TiO 2 Nanoarrays for Boosted Photoelectrochemical Water Oxidation

Photocatalytic H-2 Production on Pt/Tio2-So42- with Tuned Surface-Phase Structures: Enhancing Activity and Reducing Co Formation

Fabrication of Brookite@anatase Heterojunction TiO2via Phase Transformation from Metal Organic Frameworks for Enhanced Photocatalytic Hydrogen Evolution and TCH Degradation

Fabrication of TiO2(B)/Anatase Heterophase Junctions at High Temperature Via Stabilizing the Surface of TiO2(B) for Enhanced Photocatalytic Activity