Abstract:MS 2 morphology is strongly influenced by several parameters including the addition of a chelating agent and sulfidation temperature. In this work, we report the use of citric acid as chelating agent in order to prepare a series of WS 2 /Al 2 O 3 catalysts that were submitted to sulfidation at several temperatures. The effect of these two parameters in the morphology of the slabs was explored by means of CO adsorption at low temperature followed by IR spectroscopy (IR/CO) and later confirmed by High-Resolution Scanning Transmission Electron Microscopy coupled with High Angular Annular Dark Field detector (HR STEM - HAADF). This allowed to depict the morphology of WS 2 slabs by means of calculating the M-edge/S-edge site ratio. The use of citric acid in the preparation stage favors the increase of S-edge site concentration whereas it keeps that of M-edge sites: according to IR/CO, with an increasing amount of citric acid, the WS 2 morphology progressively changes from a slightly truncated triangle exhibiting predominantly M edges to a hexagon with both M edge and S edge. In addition, HR STEM-HAADF demonstrated that the addition of citric acid in the impregnation step of W catalysts considerably reduces the size of WS 2 nanoparticles increasing their dispersion degree. The morphology of the WS 2 plates on the activated WS 2 /Al 2 O 3 catalyst with a typical sulfidation temperature range (573–673 K) was detected to be a truncated triangle exposing both the M-edge and the S-edge. Furthermore, the IR/CO results indicate that the degree of truncation (ratio of S-edge/M-edge) of WS 2 slabs gradually rises with the increasing sulfidation temperature. However, the most determining factor for a modification of the morphology of the slabs turns out to be the presence of citric acid as a chelating agent and not the sulfidation temperature. This change in morphology (i.e., change of S-edge/M-edge ratio) is a key factor for catalytic performance, since the M-edge and the S-edge show different reactivity in hydrodesulfurization (HDS) reactions. Notably, it was also found that the addition of citric acid not only improves the catalytic activity but also the stability of the catalysts, giving the best performance in concentrations higher than (CA/W = 1).

IR spectroscopy evidence of MoS 2 morphology change by citric acid addition on MoS 2 /Al 2 O 3 catalysts – A step forward to differentiate the reactivity of M-edge and S-edge

Catalytic Characteristics of Active Corner Sites in CoMoS Nanostructure Hydrodesulfurization – A Mechanism Study Based on DFT Calculations

Infrared Spectroscopic Evidence of WS2 Morphology Change With Citric Acid Addition and Sulfidation Temperature

Effect of High Pressure Sulfidation on the Morphology and Reactivity of MoS2 Slabs on MoS2/Al2O3 Catalyst Prepared with Citric Acid

Oxygen Effects on the Structure and Hydrogenation Activity of the MoS2 Active Site: A Mechanism Study by DFT Calculation

Ir Spectroscopic Evidence for Mos2 Morphology Change with Sulfidation Temperature on Mos2/Al2o3 Catalyst

How the CO molar extinction coefficient influences the quantification of active sites from CO adsorption followed by IR spectroscopy? A case study on MoS2/Al2O3 catalysts prepared with citric acid

Catalysis by Sulfides: Advanced IR/CO Spectroscopy for the Identification of the Most Active Sites in Hydrodesulfurization Reactions

New Insight into the Support Effect on HDS Catalysts: Evidence for the Role of Mo-support Interaction on the MoS2 Slab Morphology

In Situ Ft-Ir Spectroscopic Studies Of Sulfur Effect On Mo2c/Al2o3 Catalyst.

Spectroscopic Identification of Active Centers and Reaction Pathways on MoS2 Catalyst for H2 Production Via Water-Gas Shift Reaction

Role of Citric Acid in Preparing Highly Active CoMo/Al2O3 Catalyst: from Aqueous Impregnation Solution to Active Site Formation

Adsorption and Reaction of Thiophene and H2S on Mo2C/Al2O3 Catalyst Studied by in Situ FT-IR Spectroscopy

Sulfur Effect on Mo2N/γ-Al2O3 Catalyst Studied by in Situ FT-IR Spectroscopy

Influence of Active Phase Structure of CoMo/Al2O3 Catalyst on the Selectivity of Hydrodesulfurization and Hydrodearomatization

On the Surface Sites of MoP/SiO2 Catalyst under Sulfiding Conditions: IR Spectroscopy and Catalytic Reactivity Studies

Identification of Co-O-Mo Active Centers on Co-Doped MoS2 Electrocatalyst

Identification of Co–O–Mo Active Centers on Co-Doped MoS<sub>2</sub> Electrocatalyst

Effect of sulfiding conditions on the hydrodesulfurization performance of the ex-situ presulfided CoMoS/γ-Al2O3 catalysts

In situ observations of an active MoS2 model hydrodesulfurization catalyst

XPS Characterization of Carbon Nanotube Supported CoMo Hydrodesulfurization Catalysts