Abstract:Reverse thermally induced separation (RTIPS) was used to obtain a separation membrane with a better internal structure for a higher water flux and a surface that could easily form a hydration layer. In comparison to the traditional modification method, this work focused on the aspect that the internal structure obtained by changing the membrane-making method provided easier adhesion conditions for the dopamine/TiO<sub>2</sub> hybrid nanoparticles (DA/TiO<sub>2</sub> HNPs) obtained by biomimetic mineralization. It provided a basis for exploring the variation in adhesion with the water bath temperature and the amount of titanium added through the study of turbidity point, SEM images, water contact angle, thermogravimetric test, EDX, AFM, XPS, FTIR and other test results. The SEM images proved that the membrane obtained through the RTIPS method had a porous surface and spongy internal structure, furthermore, additional polymers were adsorbed. Use of EDX demonstrated that biomimetic mineralization prevented the production of agglomerated titanium dioxide. XPS and FTIR spectra confirmed the introduction and immobilization of HNP aggregation. Moreover, a decrease in the surface roughness and water contact angle further suggested an improvement in the hydrophilicity of the modified membrane. The introduction of HNP at a higher water bath temperature helped increase the water flux up to ten times, moreover, the oil-water separation efficiency could still reach over 99.50%. Lastly, a cycle test of the modified membrane under the optimal conditions helped confirm that the membrane forming conditions at this time could provide a better environment for the formation of the hydrophilic layer, which was conducive to the recycling of the separation membrane. In summary, more fixed more hydrophilic particles could be obtained through the RTIPS method based on biomimetic mineralization to prevent the accumulation of titanium dioxide, thus helping improve permeability and anti-fouling of the membrane.

Polypropylene Microfiltration Membranes Modified with TiO2 Nanoparticles for Surface Wettability and Antifouling Property

Fabrication of High-Flux PTFE Hollow Fiber Membranes Through Nonionic Surfactant Infiltration Coupled with Mussel-Inspired Chemistry Coating

Hydrophilic Modified Polydopamine Tailored Heterogeneous Polyamide in Thin-Film Nanocomposite Membranes for Enhanced Separation Performance and Anti-Fouling Properties

Novel polysulfone hybrid ultrafiltration membrane prepared with TiO2-g-HEMA and its antifouling characteristics

Effect of TiO2 modified layer thickness on the properties of PVDF-TiO2 membrane

TiO 2 nanoparticle embedded PEEKWC/PEI cross-linked ultrafiltration membrane: Improvement in flux and anti-fouling properties

Achieving highly effective non-biofouling performance for polypropylene membranes modified by UV-induced surface graft polymerization of two oppositely charged monomers.

Preparation and Characterization of an Amphiphilic Polyamide Nanofiltration Membrane with Improved Antifouling Properties by Two-Step Surface Modification Method

Preparation of Nano-TiO2-Modified PVDF Membranes with Enhanced Antifouling Behaviors via Phase Inversion: Implications of Nanoparticle Dispersion Status in Casting Solutions

Titania Nanowires Coated PEI/P25 Membranes for Photocatalytic and Ultrafiltration Applications

A Stable Anti-Fouling Coating on PVDF Membrane Constructed of Polyphenol Tannic Acid, Polyethyleneimine and Metal Ion

Significantly enhanced antifouling and separation capabilities of PVDF membrane by synergy of semi-interpenetrating polymer and TiO2 gel nanoparticles

Antifouling modification of PVDF membranes via in situ mixed-charge copolymerization and TiO2 mineralization

Remarkable Anti-Fouling Performance of TiO2-Modified TFC Membranes with Mussel-Inspired Polydopamine Binding

Preparation and anti-biofouling performance of PSf/TiO2 ultrafiltration membrane by in-situ embedment approach

Enhancing Water Purification by Integrating Titanium Dioxide Nanotubes into Polyethersulfone Membranes for Improved Hydrophilicity and Anti-Fouling Performance

Polytetrafluoroethylene hollow fiber membranes with thru hydrophilic channels for enhancing water transfer and anti-oil-fouling properties

Surface Modification of Polypropylene Microfiltration Membrane by Grafting Poly(sulfobetaine Methacrylate) and Poly(ethylene Glycol): Oxidative Stability and Antifouling Capability

Perfluoro-functionalized polyethyleneimine that enhances antifouling property of nanofiltration membranes

Synergistic effects of PVDF membrane surface functionalization with polydopamine and titanium dioxide for enhanced oil/water separation and photocatalytic behavior

Superhydrophilic polyethersulfone (PES) membranes with high scale inhibition properties obtained through bionic mineralization and RTIPS