Abstract:The chemical heat sink yielded by the catalytic cracking of supercritical hydrocarbons facilitates the thermal management of hypersonic aircraft. The objective of this study was to alleviate the diffusion restriction of supercritical hydrocarbons in conventional microporous zeolite films. A dual template method involving different n (C22-6-6)/n (TPAOH) values was adopted to prepare pillared nanosheet HZSM-5 zeolite films by using seed assisted secondary growth. Compared with those of the parent nanosheet HZSM-5 zeolite film (ZN) prepared using only C22-6-6 as the structure directing agent (SDA), the zeolite film prepared using n (C22-6-6)/n (TPAOH) of 10/4 (DZN-4) after pillaring exhibited a higher surface area (525 m2 g−1) and mesoporous volume (0.453 cm3 g−1). A larger amount of TPAOH in the synthesized solution (n (C22-6-6)/n (TPAOH) < 10/6) induced the formation of a bulky microporous MFI crystal phase, thereby sacrificing the mesoporous structure. At 550 °C and 4 MPa, the DZN-4 zeolite film yielded the highest n-dodecane conversion rate (76.8%) and TOF value (130.9 s−1), due to the presence of highly accessible Brønsted acid sites and ordered mesoporous structures, leading to a heat sink of 2.99 MJ kg−1, which is 32% higher than that under ZN. Restricted secondary reactions, such as hydride transfer and aromatization, were observed in the presence of highly connected mesopores designed by pillaring, leading to high and low selectivities toward olefins and aromatic compounds, respectively. Amorphous coke was detected on the external mesopore surface of DZN-4, and the adhesive strength was significantly enhanced, resulting in a higher catalytic stability.

Synthesis of Hierarchical Porous Zeolite and Its Performance in N-Heptane Cracking

Synthesis and Physicochemical Characterization of Hierarchical ZSM-5: Effect of Organosilanes on the Catalyst Properties and Performance in the Catalytic Fast Pyrolysis of Biomass

Effect of Hierarchical ZSM-5 Zeolite Crystal Size on Diffusion and Catalytic Performance of N-Heptane Cracking

Effect of ZSM-5 zeolite porosity on catalytic cracking of n-heptane

n-Heptane catalytic cracking on hierarchical ZSM-5 zeolite: The effect of mesopores

Facile synthesis of hierarchical porous ZSM-5 zeolite with tunable mesostructure and its application in catalytic cracking of LDPE

ZSM-5@MCM-41 core–shell composite with tunable shell thickness for n -heptane catalytic cracking reaction

Synthesis of hierarchically porous ZSM-5 by solvent-evaporation route

Effect of Particle Size of Single-Crystalline Hierarchical ZSM-5 on Its Surface Mass Transfer in N-Heptane Catalytic Cracking

Synthesis and Performance of Pillared HZSM-5 Nanosheet Zeolites for N-Decane Catalytic Cracking to Produce Light Olefins

Hierarchical ZSM-5 zeolite designed by combining desilication and dealumination with related study of n-heptane cracking performance

Effects of post treatment of HZSM-5 zeolites on catalytic cracking of butene

Mesoporosity and Acidity Manipulation in ZSM‐23 and Their N‐hexadecane Hydroisomerization Performance

A Solvent Evaporation Route Towards Fabrication of Hierarchically Porous ZSM-11 with Highly Accessible Mesopores

Catalytic Cracking of N-Hexane to Light Alkene over ZSM-5 Zeolite: Influence of Hierarchical Porosity and Acid Property

Hierarchical Shell-Like ZSM-5 with Tunable Porosity Synthesized by Using a Dissolution-Recrystallization Approach.

Fabrication of the Hierarchical HZSM-5 Membrane with Tunable Mesoporosity for Catalytic Cracking of N-Dodecane

Protozeolite‐Seeded Synthesis of Single‐Crystalline Hierarchical Zeolites with Facet‐Shaped Mesopores and Their Catalytic Application in Methanol‐to‐Propylene Conversion

Synthesis of pillared nanosheet HZSM-5 zeolite films for catalytic cracking of supercritical n-dodecane

n-Heptane catalytic cracking on ZSM-5 zeolite nanosheets: Effect of nanosheet thickness

Different approaches to the synthesis of ZSM-22 zeolite with application in n-heptane cracking