Abstract:The luminescence properties of nanosized lanthanide oxide materials have attracted extensive inte- rest because of their fundamental and technological importance.Gd_2O_3,which is easily obtained due to abun- dant resource in nature,has been widely used as host material.The emission efficiency of Sm~(3+) associated with the intra-4f-shell transition is very high,and it earl emit bright light under both ultraviolet and infrared excitation.Therefore,it often plays a very important role in many luminescent materials.In this paper, Gd_2O_3:Sm~(3+) and Li~+-doped Gd_2O_3:Sm~(3+) nanocrystals were prepared by a combustion method.The pure nanocrystals were obtained after annealing at 800℃,and the crystallinity was improved with increasing annea- ling temperature.Both Gd_2O_3:Sm~(3+) and Li~+-doped Gd_2O_3:Sm~(3+) nanocrystals appeared to be cubic crystal- line phase according to the XRD results.In contrast to Gd_2O_3:Sm~(3+) which showed an irregular shape of ag- glomerated fine particles,the morphology of Li~+-doped Gd_2O_3:Sm~(3+) nanocrystals were spherical and quite regular.These particles were measured to be about 50 nm in diameter.When excited at 275 nm and 980 nm, Gd_2O_3:Sm~(3+) and Li~+-doped Gd_2O_3:Sm~(3+) nanocrystals exhibit similar emission spectra,which consist of the characteristic emission bands of the Sm~(3+) ions (~4G_(5/2)→~6H_J,J=5/2,7/2,9/2 transitions at 560,602,650 nm in the spectra) due to an efficient energy transfer from the Gd_2O_3 host lattice to the doped Sm~(3+) ions.It was found that the incorporation of Li~+ into the Gd_2O_3:Sm~(3+) nanocrystals has greatly enhanced the photolumi- nescence intensity of Sm~(3+) in both photoluminescence and upconversion emission.The highest emission inten- sity was observed with Gd_(1.83)Li_(0.15)Sm_(0.02)O_3,whose brightness was increased by a factor about 7.0 in compari- son with that of Gd_2O_3:Sm~(3+).As we all known that defects of the surface of the nanoparticles,which provide non-radiation recombination routes for electrons and holes,often act as non-radiative centers and has great in- fluence on luminescent properties.It can be suggested that the incorporation of Li~+ can greatly decrease the deficiencies and oxygen vacancies.That is,the defects and oxygen vacancies of the surface of nanoparticles decreased at first when Li~+ content was lower,which decreased the luminescence quenching centers and in- creased the crystallinity,thereby enhanced the emission intensity.A lot of defects could be induced in the sys- tem with a gradual increase of Li~+ content.This will destroy the crystallinity and thus lead to the luminescence quenching.In conclusion,this paper reported the correlation between the morphology,structure and optical behaviors on Gd_2O_3:Sm~(3+) nanocrystals doped with Li~+ Li~+ doping at a low content significantly improved the morphology of phosphors and strongly enhanced the luminescent properties.

Luminescence Studies of Sm3+ Single-Doped and Sm3+, Dy3+ Co-Doped Nagdtio4 Phosphors

Preperation and Photoluminescent Properties of Ca2AlSi3O2N5:Sm3+ Phosphor

Spectroscopy analysis and optical transition property of GdNbTiO6: Eu3+, Sm3+ phosphor

Synthesis and Luminescence Properties of a Novel Red SrMoO4:Sm3+,R+ Phosphor

Warm-white luminescence of Dy3+ and Sm3+ co-doped NaSrPO4 phosphors through energy transfer between rare earth ions

Enhanced Photoluminescense of Gd2O3∶ Sm3+ Nanocrystals by Li+ Doping

Effect of Gd3+, La3+, Lu3+ Co-Doping on the Morphology and Luminescent Properties of NaYF4:Sm3+ Phosphors

Structural, photoluminescence and energy transfer investigations of novel Dy3+ → Sm3+ co-doped NaCaPO4 phosphors for white-light-emitting diode applications

Luminescence and optical properties of sodium germanate glasses doped with Sm3+ ions

Energy transfer in Sm3+/Eu3+ doped Li6Gd(BO3)3 orange-red phosphor

Enhanced color rendering index and thermal stability of Ca2GdNbO6: Dy3+ phosphors by co-doping Sm3+ ions

Upconversion Luminescence Properties of Ho3+/Tm3+/Yb3+ Co-doped NaGd(MO4)2 Prepared by Hydrothermal Method

Photoluminescence characteristics of Sm3+ doped Na13Sr2Ta2(PO4)9 as new orange-red emitting phosphors

Structural and Photoluminescence Properties of a Novel Ba2GdNbO6: Sm3+ Phosphor

Photoluminescence in singly and co-doped K3Gd(PO4)2:Sm3+, Eu3+ phosphate phosphors

Luminescence properties and energy transfer of a red-emitting Ca3 (PO4)2:Sm3+, Eu3+ phosphor

Influence of inorganic salt on morphology, particle size, and luminescence properties of lanthanide ions doped Na0.5Gd0.5MoO4 microcrystals

Adjusting luminescence properties of ZnAl2O4:Mn2+(Mn4+), Li+ phosphors through cation substitution

Luminescent Properties of Li+ Doped Nanosized Y2O3:Eu

Persistent Luminescence in Rare Earth Ion-Doped Gadolinium Oxysulfide Phosphors

Enhancing luminescence intensity and improving thermostability of red phosphors Li3Ba2La3(WO4)8:Eu3+ by co-doping with Sm3+ ions