The Studies of Nanocrystalline Ni0.7Mn0.3NdxFe2–xO4 () Ferrites

Lijun Zhao,Hua Yang,Lianxiang Yu,Yuming Cui,Xueping Zhao,Yu Yan,Shouhua Feng
DOI: https://doi.org/10.1016/j.physleta.2004.09.010
IF: 2.707
2004-01-01
Physics Letters A
Abstract:Nanocrystalline Ni0.7Mn0.3NdxFe2–xO4 ferrites with x values ranging from 0.00 to 0.10, in step of 0.02, have been prepared by the emulsion method. The structure and the morphology of ferrite nanoparticles were measured using X-ray diffractometer (XRD), transmission electron microscope (TEM) and Mössbauer spectra. It is shown that the structure of Ni0.7Mn0.3NdxFe2–xO4 ferrites nanoparticles is single spinel structure. The average crystallite sizes of the samples calculated using Scherrer' relationship are almost identical with the observed diameter from the image of TEM. The magnetic properties of the samples were tested by a vibrating sample magnetometer (VSM) at room temperature. The nanoparticles of the samples have superparamagnetism when particle sizes are about 10 nm.
What problem does this paper attempt to address?