Abstract:Superplasticizers, polyacrylate latexes and asphalt emulsions were employed to investigate the influences of chemical admixtures with different sizes on the pore structure and impermeability of hardened cement pastes. With different admixture types and contents, pore structure and impermeability of specimens cured for 28 days were tested by mercury intrusion porosimetry and alternating current impedance, respectively. Scanning electron microscopy was also used to observe the microstructure of fresh and hardened pastes. The results show that, porosity, average pore size and inkbottle pores volume in the hardened cement pastes as well as permeability presented slight decrease with the increase in the content of superplasticizers. For the specimens with low latex content, the pore size in the hardened cement paste remained unchanged, or was coarsened, and the compactness and impermeability declined; for those with high latex content, the pore size was refined and compactness and impermeability were enhanced. Both of the compactness and impermeability increased with the increase in asphalt emulsion content. At the same content, the latex Ll, having smaller particle size was more effective than latex L2 and, the anionic asphalt emulsion was more effective than cationic asphalt emulsion on improving pore structure and impermeability, respectively. It was accepted that chemical admixtures were able to improve the flowability of fresh paste by enhancing the dispersion of cement grains, further the effects were extended to affect the pore structure and impermeability of hardened one. Meanwhile, the polymer was also effective to compact the interfacial zone between phases by filling up the pore space, which would lead to more compact structure of hardened paste. For the same type of chemical admixture at low content, the pore structure and impermeability were mainly influenced by the dispersion of cement grains, while at high content, the filling effect become dominant. For different types of chemical admixtures with the same filling effect, the better dispersion of cement grains would result in finer pore structure and higher impermeability.

Influences of PCE Superplasticizer on the Pore Structure and the Impermeability of Hardened Cementitious Materials

Influence of Superplasticizers on Early Age Drying Shrinkage of Cement Paste with the Same Consistency

Effects of PCE on the Dispersion of Cement Particles and Initial Hydration

Effect of anchoring groups of polycarboxylate ether superplasticizer on the adsorption and dispersion of cement paste containing montmorillonite

Influences Of Chemical Admixtures With Different Sizes On Pore Structure And Impermeability Of The Hardened Cement

Investigating the effect of polycarboxylate-ether based superplasticizer on the microstructure of cement paste during the setting process

Retardation effect of PCE superplasticizers with different architectures and their impacts on early strength of cement mortar

Effect of the structure of macromonomer in polycarboxylate superplasticizer on viscosity and workability of concrete

Effects and Mechanism of Hyperbranched Phosphate Polycarboxylate Superplasticizers on Reducing Viscosity of Cement Paste

Influences of superplasticizer, polymer latexes and asphalt emulsions on the pore structure and impermeability of hardened cementitious materials

Adsorption and dispersion capability of polycarboxylate-based superplasticizers: a review

Influences of PCE Superplasticizers with Varied Architectures on the Formation and Morphology of Calcium Hydroxide Crystals

Influence of Sand-Cement Ratio and Polycarboxylate Superplasticizer on the Basic Properties of Mortar Based on Water Film Thickness

Interaction mechanisms between polycarboxylate superplasticizers and cement, and the influence of functional groups on superplasticizer performance: a review

The acceleration effect of nano C-S-H-PCE on the microstructure formation and evolution at early age of cement paste

Effects of polycarboxylate superplasticizer on rheological properties and early hydration of natural hydraulic lime

Effects of a polycarboxylate superplasticiser on the rheological properties of a Portland-sulphoaluminate cement composite slurry

Study on rheological, adsorption and hydration properties of cement slurries incorporated with EPEG-based polycarboxylate superplasticizers

Study on the Influence of Early Strength Polycarboxylate Superplasticizer on Early Performance of Concrete

Effect of Functional Superplasticizers on Concrete Strength and Pore Structure

Effect of Molecular Structure of Maleic Anhydride, Fumaric Acid – Isopentenyl Polyoxyethylene Ether Based Polycarboxylate Superplasticizer on Its Properties in Cement Pastes