Abstract:With phenolic resin as carbon source, ethylene glycol as solvent and pore-forming agent, and silicon monoxide as pore-forming agent and silicon source, a kind of light hierarchical porous silicon carbide (SiC) ceramics with adjustable pores was prepared by gelcasting, carbonization and carbothermal reduction. With the addition of silicon monoxide in the green body from 13 to 49 % , the porosities increased from 66 to 89 % , the densities and thermal conductivity are as low as 0.36 g·cm ¹ 3 and 0.29 W·m ¹ 1 ·K ¹ 1 . The macropores are mainly determined by the addition of silica particle size, which increases from 9.2 to 39.5 % , while the micropores and mesopores, ranging from 56.8 to 49.5 % , are mainly determined by the pyrolysis of resin carbon source. When the porosity of porous SiC is 75 % , the compressive strength of 7.83 MPa can be reached. The prepared porous SiC ceramics possessed light, good thermal insulation and other properties, which can be further improved by changing the shape and size of the added SiO particles. In addition, di ﬀ erent from using polycarbosilane as preceramic polymer, the porous SiC ceramics with complex shape and uniform microstructure can be prepared via gelcasting, which will reduce the production costs and broaden its application.

Characterization and Application of Porous Ti3SiC2 Ceramic Prepared Through Reactive Synthesis

In-situ Grown Columnar Mullite Reinforced SiC Porous Ceramic Membrane Support with Excellent Mechanical Performance and Corrosion Resistance: Using TiO2 As the Key to Form Columnar Mullite

Porous TiFe2 intermetallic compound fabricated via elemental powder reactive synthesis

Fabrication and characterization of pure porous Ti3SiC2 with controlled porosity and pore features

The Thermal, Electrical and Mechanical Properties of Porous Α-Sic Ceramics Bonded with Ti3SiC2 and Β-Sic Via Low Temperature In-Situ Reaction Sintering

Preparation and characterization of porous carbon–titania nanocomposite films as solar selective absorbers

Effect of Different Particle Sizes and Pore-Making Agent Ratio on Properties of SiC Porous Ceramics

Template‐Synthesized Porous Silicon Carbide As an Effective Host for Zeolite Catalysts

Synthesis and Characterization of Hierarchical Titania-Silica Monolith

Fabrication and Characterization of Hierarchical Porous SiC Ceramics Via Gelcasting and Carbothermal Reduction Between Carbon and SiO

Porous 2h‐silicon Carbide Ceramics Fabricated by Carbothermal Reaction Between Silicon Nitride and Carbon

Preparation and characterization of Ti3SiC2 powder

Correlation between permeation performance and structural evolution of Al-doped lamellar porous Ti 3 SiC 2 through freeze casting

Fabrication and Characterization of SiC-Based Porous Ceramic Used for High Temperature Filtration Supporter

Self-propagation High-temperature Synthesis of Porous TiB2-TiC Multiphase Ceramics

Porous Titanium Carbide Ceramics Fabricated by Coat-Mix Process

Preparation and Characterization of Hierarchically Porous Monolithic TiO2

Review of porous intermetallic compounds by reactive synthesis of elemental powders

Reactive Synthesis of Porous Cu3si Compound

Fabrication of Porous Al2TiO5-Al2O3 Ceramics Using Al2O3 Hollow Spheres Coated with TiO2 Sol

Preparation, Characterization Analysis and Application of Porous TiO_2/TiC Shell -Core Composite