Abstract:The tempering process of plate glass involves rapidly cooling the high-temperature glass using an array of impinging air jets, inducing desired stress during cooling. Consequently, the formation of tempering stress results from the coupled interaction among flow, heat transfer, and stress. However, most previous studies have commonly neglected the influence of the flow field by assuming a uniform and constant distribution of heat transfer coefficients at different positions on the glass plate, which deviates from actual situations. This study employed a fluid-thermal-structural coupled simulation approach to predict the non-uniform residual stress distribution in tempered glass and investigate the interaction mechanisms among flow, heat transfer, and stress. Simultaneously, to validate the reliability of the method and model, this study experimentally investigated the single-nozzle jet impingement cooling for glass tempering. The study concluded that the simulation results were consistent with the experiment. Subsequently, a comparative analysis was performed between the fluid-thermal-structural coupled simulation results based on real boundary conditions and the thermal-structural coupled simulation results based on ideal uniform heat transfer coefficient boundary conditions. The results revealed non-uniform distributions of both heat transfer coefficient and temperature due to varying localized flow characteristics. Consequently, the ratio of surface compressive stress to internal tensile stress along the width direction of the glass was not a fixed value but ranged from 1.63 to 2.38. Furthermore, significant differences were observed in the stress distribution under the simulations of fluid-thermal-structural coupling and thermal-structural coupling. Therefore, it is recommended to employ the fluid-thermal-structural coupling method when predicting localized stress distribution.

Experimental study on critical breaking stress of float glass under elevated temperature

Experimental Study on Crack of Float Glass with Different Thicknesses Exposed to Radiant Heating

Experimental and Numerical Study of Window Glass Breakage with Varying Shaded Widths under Thermal Loading

A Stochastic Analysis of Glass Crack Initiation under Thermal Loading

Finite Element Analysis on Non-Isothermal Glass Molding

Thermal Shock Effect on the Glass Thermal Stress Response and Crack Propagation

The Breakage of Float Glass with Four-Edge Shading under the Combined Effect of Wind Loading and Thermal Loading

EXPERIMENTAL RESEARCH ON IMPACT BEHAVIOR OF CONCRETE-FILLED STEEL TUBE AT ELEVATED TEMPERATURES

Experimental Investigation on Glass Cracking for Wind Load Combined with Radiant Heating

Experimental Study on Thermal Breakage of Four-Point Fixed Glass Façade

Thermal Performance of Exposed Framing Glass Façades in Fire

Maximum Temperature to Withstand Water Film for Tempered Glass Exposed to Fire

Crack Evolution Process of Window Glass under Radiant Heating

Determination of Critical Breakage Conditions for Double Glazing in Fire

Coupled fluid-thermal-structural analysis during the air cooling for glass tempering

Experimental investigation into the effect of elevated temperatures on the fracture strength of soda-lime-silica glass

The fracture behavior of hollow glass under heating condition

Chemical strengthening of high aluminosilicate glasses and experimental fitting

Investigation of the Thermal Response and Breakage Mechanism of Point-Supported Glass Facade under Wind Load

033 Crack initiation and path prediction of float glass with various constrain conditions under thermal loading

Temperature and Thermal Stress Simulation of Window Glass Exposed to Fire