Abstract:In this study, pure cobalt oxide (Co 3 O 4 ) nanoparticles were synthesized using a simple hydrothermal approach. The effect of the reducing agent and reaction temperatures of the prepared products were examined. Co 3 O 4 is formed in the as-synthesized sample, at reaction temperature 190 °C was observed in the XRD pattern. The XPS survey scan spectrum showed the distinctive peaks of the Co and O elements and their valence states. FESEM and HRTEM revealed the particles as cubical in nature. Peak associated with the elements Co and O on the EDAX spectrum demonstrated the purity of the nanoparticles. Three electrode setups were used to measure the electrochemical properties of the synthesized nanoparticles. DTA curve corresponding exothermic peak at 225 °C and the crystallization of the final product was attributed for the third weight loss of 1.5 % in the temperature range of 280 °C to 450 °C. Formation of Co 3 O 4 was confirmed by the observed XRD diffraction peaks at 2 θ = 36.83°, 59.82°, and 65.30°, which correspond to h k l planes (311), (511) and (440), respectively. The high-resolution Co2p spectra showed two prominent spin-orbital peaks, 2p 1/2 and 2p 3/2 , at 796.37 eV and 781.81 eV, respectively. The increase in temperature causes the particle size to grow ranges between 20 and 70 nm and the average particle size distribution in the TEM image is 42 nm. The integral area of the CV curve was measured during the CV measurement and as the as-prepared Co 3 O 4 electrode displays specific capacitance values of 154, 126, 81, 65, and 49 Fg −1 at various scan rates of 10, 20, 50, 70, and 100 mVs −1 , respectively.

One-pot facile synthesis of cobalt oxide nanocubes and their magnetic properties

Porous Co3o4 Microcubes: Hydrothermal Synthesis, Catalytic and Magnetic Properties

One-pot synthesis and magnetic properties of hollow Fe<sub>70</sub>Co<sub>30</sub> nanospheres

Novel three-dimensional Co3O4 dendritic superstructures: Hydrothermal synthesis, formation mechanism and magnetic properties

Studies on the magnetism of cobalt ferrite nanocrystals synthesized by hydrothermal method

One-pot Synthesis of CoFe–Fe3O4 Nanocomposites with Tunable Magnetic Properties and Long Term Stability

Controlled synthesis and anomalous magnetic properties of relatively monodisperse CoO nanocrystals.

Facile hydrothermal synthesis of ZnCo2O4 nanostructures: controlled morphology and magnetic properties

Functionalization of carbon nanotubes with magnetic nanoparticles: general nonaqueous synthesis and magnetic properties.

Studies on the nanocrystalline Co3O4 by wet synthesis and its microstructure

Shape-controlled synthesis and properties of uniform spinel cobalt oxide nanocubes

Facile hydrothermally grown cobalt oxide (Co 3 O 4 ) nanostructures and their electrochemical performances

Hydrothermal Synthesis of Cobalt Particles with Hierarchy Structure and Physicochemical Properties

Synthesis And Magnetic Properties Of Zn1-Xcoxo Nanorods

Simplified Synthesis of Single-Crystalline Magnetic CoFe2O4 Nanorods by a Surfactant-Assisted Hydrothermal Process

Chemical Synthesis, Structure and Magnetic Properties of Co Nanorods Decorated with Fe3O4 Nanoparticles

Synthesis and characterization of ferromagnetic cobalt nanospheres, nanodiscs and nanocubes

Phase- and Size-Dependent Optical and Magnetic Properties of CoO Nanoparticles

Formation of Co 3 O 4 Nanotubes and the Magnetic Behaviour at Low Temperature

Micelle-assisted hydrothermal synthesis of the uniform Co3O4 nanorods and its chemoluminescence properties of CO oxidation

Synthesis and Magnetic Properties of Cobalt Ferrite (CoFe2O4) Nanoparticles Prepared by Wet Chemical Route